沙伯基础高流动耐冲ABS CYCOLAC MG94F
Density | 1.04 | g/cm | ISO 1183 |
Melt Mass-Flow Rate (MFR) | |||
230°C/3.8 kg | 12 | g/10 min | ASTM D1238 |
220°C/5.0 kg | 12 | g/10 min | ISO 1133 |
Melt Volume-Flow Rate (MVR)(220°C/10.0 kg) | 39 | cm/10min | ISO 1133 |
Molding Shrinkage - Flow2 | 0.50 to 0.70 | % | Internal Method |
Water Absorption(Equilibrium, 23°C, 50% RH) | 0.16 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
Rockwell Hardness(R-Scale) | 129 | ISO 2039-2 | |
Ball Indentation Hardness(H 358/30) | 95.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus | 2400 | MPa | ISO 527-2/1 |
Tensile Stress | |||
Yield | 40.0 | MPa | ISO 527-2/5 |
Yield | 45.0 | MPa | ISO 527-2/50 |
Break | 35.0 | MPa | ISO 527-2/5,ISO 527-2/50 |
Tensile Strain | |||
Yield | 2.0 | % | ISO 527-2/5 |
Yield | 2.2 | % | ISO 527-2/50 |
Break | 35 | % | ISO 527-2/5 |
Break | 45 | % | ISO 527-2/50 |
Flexural Modulus3 | 2450 | MPa | ISO 178 |
Flexural Stress3,4 | 65.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
Charpy Notched Impact Strength5 | ISO 179/1eA | ||
-30°C | 10 | kJ/m | |
23°C | 23 | kJ/m |
ABS物料性能
1.综合性能较好,冲击强度较高,化学稳定性,电性能良好；
2.与372有机玻璃的熔接性良好,制成双色塑件,且可表面镀铬,喷漆处理；
3.有高抗冲、高耐热、阻燃、增强、透明等级别；
4.流动性比HIPS差一点，比PMMA、PC等好，柔韧性好；
5.适于制作一般机械零件,减磨***零件,传动零件和电讯零件。