Density(23°C) | 1.20 | g/cm | *** 1183 |
Melt Volume-Flow Rate (MVR)(220°C/10.0 kg) | 8.00 | cm/10min | *** 1133 |
Molding Shrinkage - Flow(23°C) | 0.10 to 0.40 | % | *** 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
Rockwell Hardness(R-Scale, 23°C) | 117 | *** 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus(23°C) | 7000 | MPa | *** 527-2 |
Tensile Stress(Break, 23°C) | 96.0 | MPa | *** 527-2 |
Flexural Modulus3(23°C) | 6200 | MPa | *** 178 |
Flexural Stress3(23°C) | 126 | MPa | *** 178 |
| Impact | Nominal Value | Unit | Test Method |
Charpy Notched Impact Strength | *** 179 | ||
-30°C | 3.0 | kJ/m | |
23°C | 7.0 | kJ/m |
| Thermal | Nominal Value | Unit | Test Method |
Heat Deflection Temperature(1.8 MPa, Unannealed) | 101 | °C | *** 75-2/Af |
CLTE - Flow | 4.0E-5 | cm/cm/°C | *** 11359-2 |
| Flammability | Nominal Value | Test Method | |
Flame Rating(1.5 mm) | HB | UL 94 |
ABS树脂是五大合成树脂之一，其抗冲击性、耐热性、耐低温性、耐化学药品性及电气性能优良，还具有易加工、制品尺寸稳定、表面光泽性好等特点，容易涂装、着色，还可以进行表面喷镀金属、电镀、焊接、热压和粘接等二次加工，***应用于机械、汽车、电子电器、仪器仪表、纺织和建筑等工业领域，是一种用途极广的热塑性工程塑料。ABS通常为浅黄色或乳白色的粒料非结晶性树脂。ABS为使用******非通用塑料之一。