Density / Specific Gravity(Natural) | 1.16 | g/cm | ASTM D792,ISO 1183 |
Melt Mass-Flow Rate (MFR)(200°C/5.0 kg) | 3.3 | g/10 min | ASTM D1238,ISO 1133 |
Molding Shrinkage | |||
Flow : 3.20 mm | 0.30 to 0.60 | % | ASTM D955 |
Across Flow : 3.20 mm | 0.30 to 0.60 | % | ASTM D955 |
Across Flow : 2.00 mm | 0.30 to 0.60 | % | ISO 294-4 |
Flow : 2.00 mm | 0.30 to 0.60 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
Rockwell Hardness | |||
R-Scale | 99 | ASTM D785 | |
R-Scale | 103 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus | |||
--3 | 1600 | MPa | ASTM D638 |
-- | 2100 | MPa | ISO 527-2/50 |
Tensile Strength | |||
Yield3 | 39.0 | MPa | ASTM D638 |
Yield | 44.0 | MPa | ISO 527-2/50 |
Break3 | 25.0 | MPa | ASTM D638 |
Break | 31.0 | MPa | ISO 527-2/50 |
Flexural Modulus | |||
--4 | 1900 | MPa | ASTM D790 |
--5 | 2200 | MPa | ISO 178 |
Flexural Strength | |||
--4 | 54.0 | MPa | ASTM D790 |
--5 | 68.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
Charpy Notched Impact Strength6(23°C) | 18 | kJ/m | ISO 179/1eA |
Notched Izod Impact | |||
23°C, 3.18 mm | 170 | J/m | ASTM D256 |
23°C, 6.35 mm | 150 | J/m | ASTM D256 |
23°C6 | 20 | kJ/m | ISO 180/1A |
塑料ABS***、无味，外观呈象牙色半透明，或透明颗粒或粉状。密度为1.05~1.18g/㎝3,收缩率为0.4%~0.9%,弹性模量值为2Gpa,泊松比值为0.394，吸湿性<1%，熔融温度217~237℃，热分解温度>250℃。
塑料ABS有优良的力学性能，其冲击强度极好，可以在极低的温度下使用；塑料ABS的***性优良，尺寸稳定性好，又具有耐油性，可用于中等载荷和低转速下的轴承。ABS的耐蠕变性比PSF及PC大，但比PA及POM小。