奥地利SAX ABS SAXALAC 820 LE高流动低气味
Density | 1.04 | g/cm³ | |
Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 20 | cm³/10min | *** 1133 |
Molding Shrinkage | 0.50 to 0.80 | % | |
Moisture Content | <0.20 | % | Internal Method |
Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus (23°C) | 2300 | MPa | *** 527-1 |
Tensile Stress (23°C) | 45.0 | MPa | *** 527-2 |
Tensile Strain (Break, 23°C) | 23 | % | *** 527-2 |
Impact | Nominal Value | Unit | Test Method |
Charpy Notched Impact Strength | *** 179/1eA | ||
-30°C | 9.0 | kJ/m² | |
23°C | 25 | kJ/m² | |
Charpy Unnotched Impact Strength | *** 179/1eU | ||
-30°C | 60 | kJ/m² | |
23°C | 100 | kJ/m² | |
Notched Izod Impact Strength | *** 180/1A | ||
-30°C | 8.0 | kJ/m² | |
23°C | 21 | kJ/m² | |
Unnotched Izod Impact Strength | *** 180 | ||
-30°C | 65 | kJ/m² | |
23°C | 100 | kJ/m² |
Thermal | Nominal Value | Unit | Test Method |
Deflection Temperature Under Load 2 (1.8 MPa, Unannealed, 60.0 mm Span) | 81.0 | °C | *** 75-2/A |
Vicat Softening Temperature | 100 | °C | *** 306/B50 |