低翘曲高耐热LCP SUMIKASUPER E6807LHF
Density / Specific Gravity | 1.67 | g/cm | ASTM D792 |
Molding Shrinkage | Internal Method | ||
Across Flow | 0.63 | % | |
Flow | 0.11 | % | |
Water Absorption(Saturation) | 0.020 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
Rockwell Hardness(R-Scale) | 101 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
Tensile Strength | 134 | MPa | ASTM D638 |
Tensile Elongation(Break) | 4.5 | % | ASTM D638 |
Flexural Modulus | ASTM D790 | ||
23°C | 12100 | MPa | |
200°C | 4500 | MPa | |
Flexural Strength | ASTM D790 | ||
23°C | 145 | MPa | |
200°C | 29.0 | MPa | |
Shear Strength | 53.0 | MPa | ASTM D732 |
Poisson&＃39;s Ratio | 0.41 | ASTM D785 | |
| Impact | Nominal Value | Unit | Test Method |
Notched Izod Impact(6.40 mm) | 120 | J/m | ASTM D256 |
Unnotched Izod Impact(6.40 mm) | 340 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
Deflection Temperature Under Load(1.8 MPa, Unannealed) | 269 | °C | ASTM D648 |
CLTE | Internal Method | ||
Flow : 150°C | 1.0E-5 | cm/cm/°C | |
Transverse : 150°C | 6.3E-5 | cm/cm/°C | |
Thermal Conductivity | 0.56 | W/m/K | JIS R2618 |