日本东丽35%玻矿LCP SIVERAS LX70T35H

Density / Specific Gravity	1.68	g/cm	ASTM D792
Molding Shrinkage2			Internal Method
Across Flow : 1.00 mm	0.45	%
Flow : 1.00 mm	0.030	%
Outdoor Suitability	f2		UL 746C

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength	130	MPa	ASTM D638
Tensile Elongation(Break)	3.5	%	ASTM D638
Flexural Modulus	11500	MPa	ASTM D790
Flexural Strength	155	MPa	ASTM D790
Impact	Nominal Value	Unit	Test Method
Notched Izod Impact	65	J/m	ASTM D256

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load(1.8 MPa, Unannealed)	240	°C	ASTM D648
CLTE - Flow	8.0E-6 to 1.9E-5	cm/cm/°C	ASTM D696

Electrical	Nominal Value	Test Method
Comparative Tracking Index (CTI)	PLC 3	UL 746
Flammability	Nominal Value	Test Method
Flame Rating(0.38 mm)	V-0	UL 94

热致液晶聚合物还可与多种塑料制成聚合物共混材料，这些共混材料中液晶聚合物起到玻纤增强的作用，可以大大提高材料的强度、刚性及耐热性等。F：LCP塑胶原料密度为1.4~1.7g/cm3。液晶聚合物具有高强度，高模量的力学性能，由于其结构特点而具有自增强性，因而不增强的液晶塑料即可达到甚至超过普通工程塑料用***之几十玻璃纤维增强后的机械强度及其模量的水平；如果用玻璃纤维、碳纤维等增强，更远远超过其他工程塑料。G：LCP液晶聚合物还具有优良的热稳定性、耐热性及耐化学药品性，对大多数塑料存在的蠕变缺点，液晶材料可忽略不计，而且***、减磨性均***。H：LCP塑胶原料具有优良的电绝缘性能。其介电强度比一般工程塑料高，耐电弧性良好。作为电器应用制件，在连续使用温度200~300℃时，其电性能不受影响。而间断使用温度可达316℃左右。I：LCP塑胶原料具有突出的***性能，LCP制品在浓度为90%的酸及浓度为50%的碱存在下不会受到侵蚀，对于工业溶剂、燃料油、洗涤剂及热水，接触后不会被溶解，也不会引起应力开裂。