化学成分允许偏差 | ||||||||
牌号 | 化学成分(熔炼分析)%(质量分数) | |||||||
C 不大于 | Mn 不大于 | P 不大于 | S 不大于 | Alt 不大于 | Si 不大于 | Ti 不大于 | Nb 不大于 | |
HC180P | 0.05 | 0.6 | 0.08 | 0.025 | 0.015 | |||
B180P2 | 0.08 | 0.8 | 0.12 | 0.025 | 0.015 | |||
HC220P | 0.07 | 0.7 | 0.08 | 0.025 | 0.015 | |||
B220P2 | 0.10 | 1.0 | 0.12 | 0.025 | 0.015 | |||
HC260P | 0.08 | 0.7 | 0.10 | 0.025 | 0.015 | |||
HC300P | 0.10 | 0.7 | 0.12 | 0.025 | 0.015 | |||
HC220I | 0.06 | 0.8 | 0.04 | 0.020 | 0.015 | |||
HC260I | 0.08 | 1.2 | 0.10 | 0.020 | 0.015 | |||
B170P1 | 0.006 | 1.0 | 0.08 | 0.025 | 0.015 | ≤0.20 a | ||
HC180Y | 0.01 | 0.8 | 0.08 | 0.025 | 0.010 | ≤0.12 b | ||
B210P1 | 0.008 | 1.2 | 0.10 | 0.025 | 0.015 | ≤0.20 a | ||
HC220Y | 0.01 | 1.4 | 0.10 | 0.025 | 0.010 | ≤0.12 b | ||
B250P1 | 0.008 | 1.2 | 0.12 | 0.025 | 0.015 | ≤0.20 a | ||
HC260Y | 0.01 | 2.0 | 0.12 | 0.025 | 0.01 | ≤0.12 b | ||
B140H1 | 0.006 | 0.4 | 0.04 | 0.020 | 0.015 | ≤0.10c | ||
B180H1 | 0.008 | 1.0 | 0.08 | 0.020 | 0.015 | ≤0.10c | ||
B180H2 | 0.06 | 0.7 | 0.08 | 0.025 | 0.015 | |||
HC180B | 0.06 | 0.7 | 0.06 | 0.030 | 0.015 | 0.5 | ||
HC220B | 0.08 | 0.7 | 0.085 | 0.030 | 0.015 | 0.5 | ||
HC260B | 0.1 | 1.0 | 0.1 | 0.030 | 0.015 | 0.5 | ||
HC300B | 0.1 | 1.0 | 0.12 | 0.030 | 0.015 | 0.5 | ||
HC260LA | 0.1 | 1.0 | 0.025 | 0.025 | 0.015 | 0.5 | 0.15d | |
HC300LA | 0.12 | 1.4 | 0.025 | 0.025 | 0.015 | 0.5 | 0.15d | 0.09d |
HC340LA | 0.12 | 1.5 | 0.025 | 0.025 | 0.015 | 0.5 | 0.15d | 0.09d |
B340LA | 0.12 | 1.0 | 0.03 | 0.030 | 0.020 | 0.09d | ||
HC380LA | 0.12 | 1.6 | 0.025 | 0.025 | 0.015 | 0.5 | 0.15d | 0.09d |
HC420LA | 0.12 | 1.6 | 0.025 | 0.025 | 0.015 | 0.5 | 0.15d | 0.09d |
B410LA | 0.2 | 2.0 | 0.03 | 0.030 | 0.020 | 0.09d | ||
HC460LA | 0.14 | 1.8 | 0.025 | 0.025 | 0.015 | 0.5 | 0.15d | 0.09d |
HC500LA | 0.14 | 1.8 | 0.025 | 0.025 | 0.015 | 0.6 | 0.15d | 0.09d |
HC550LA | 0.14 | 1.8 | 0.025 | 0.025 | 0.015 | 0.6 | 0.15d | 0.09 |
a 允许用Nb 部分或全部代替Ti,此时Nb 和/或Ti 的总含量应不大于0.20%。 | ||||||||
b 允许用Nb 部分或全部代替Ti,此时Nb 和/或Ti 的总含量应不大于0.12%。 | ||||||||
c 可用Ti 部分或全部代替Nb,此时Ti 和/或Nb 的总含量≤0.10%。 | ||||||||
d 可以单独或复合添加Ti 和Nb。也可添加V 和B,此时这些合金元素的总含量≤0.22%。 |