Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 0.935 g/cc | 0.0338 lb/in³ | ASTM D1505 |
Melt Flow | 0.50 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.50 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
Mechanical Properties | Metric | English | Comments |
Film Tensile Strength at Yield, MD | 16.5 MPa | 2400 psi | ASTM D882 |
Film Tensile Strength at Yield, TD | 19.3 MPa | 2800 psi | ASTM D882 |
Film Elongation at Break, MD | 550 % | 550 % | ASTM D882 |
Film Elongation at Break, TD | 790 % | 790 % | ASTM D882 |
Puncture Energy | 2.26 J | 1.67 ft-lb | ExxonMobil Method |
Elmendorf Tear Strength MD | 20 g | 20 g | ASTM D1922 |
Elmendorf Tear Strength TD | 610 g | 610 g | ASTM D1922 |
Dart Drop Test | 70.0 g | 0.154 lb | ASTM D1709A |
Film Tensile Strength at Break, MD | 57.9 MPa | 8400 psi | ASTM D882 |
Film Tensile Strength at Break, TD | 46.2 MPa | 6700 psi | ASTM D882 |
1% Secant Modulus, MD | 427 MPa | 62000 psi | ASTM D882 |
1% Secant Modulus, TD | 517 MPa | 75000 psi | ASTM D882 |
Thermal Properties | Metric | English | Comments |
Melting Point | 123 °C | 253 °F | Peak; ExxonMobil Method |
Vicat Softening Point | 119 °C | 246 °F | ASTM D1525 |
Optical Properties | Metric | English | Comments |
Haze | 14 % | 14 % | ASTM D1003 |
Gloss | 40 % | 40 % | @ 45°; ASTM D2457 |