Density | 1.22 | -- | g/cm | *** 1183 |
Molding Shrinkage | *** 294-4 | |||
Across Flow | 0.70 | -- | % | |
Flow | 0.10 | -- | % | |
Water Absorption | *** 62 | |||
Saturation, 23°C | 1.1 | -- | % | |
Equilibrium, 23°C, 50% RH | 0.60 | -- | % | |
| Hardness | Dry | Conditioned | Unit | Test Method |
Shore Hardness(Shore D, 15 sec) | -- | 77 | *** 868 | |
Ball Indentation Hardness | -- | 120 | MPa | *** 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
Tensile Modulus | 6500 | 6000 | MPa | *** 527-2 |
Tensile Stress(Break) | 120 | 105 | MPa | *** 527-2 |
Tensile Strain(Break) | 6.0 | 8.0 | % | *** 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
Charpy Notched Impact Strength | *** 179/1eA | |||
-30°C | 15 | 15 | kJ/m | |
23°C | 19 | 20 | kJ/m | |
Charpy Unnotched Impact Strength | *** 179/1eU | |||
-30°C | 90 | 80 | kJ/m | |
23°C | 90 | 80 | kJ/m |
| Thermal | Dry | Conditioned | Unit | Test Method |
Heat Deflection Temperature | ||||
1.8 MPa, Unannealed | 160 | -- | °C | *** 75-2/A |
8.0 MPa, Unannealed | 90.0 | -- | °C | *** 75-2/C |
Continuous Use Temperature | ||||
--3 | 90.0 to 120 | -- | °C | *** 2578 |
--4 | 150 | -- | °C | Internal Method |
Melting Temperature5 | 178 | -- | °C | *** 11357-3 |
CLTE | *** 11359-2 | |||
Flow | 2.0E-5 | -- | cm/cm/°C | |
Transverse | 1.5E-4 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
Surface Resistivity | -- | 1.0E+12 | ohms | IEC 60093 |
Volume Resistivity | -- | 1.0E+13 | ohms·cm | IEC 60093 |
Electric Strength | -- | 35 | kV/mm | IEC 60243-1 |
Comparative Tracking Index | -- | 600 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
Flammability Classification(0.8 mm) | HB | -- | IEC 60695-11-10, -20 |