30GF热稳定PA6 Amilan CM1016G-30
¥30.50
45%玻纤PA6 Amilan CM1011G-45
¥29.50
矿物增强PA6 Amilan CM1001R
¥32.50
无卤阻燃PA6 Amilan CM1014-V0
¥34.50
***PA6 Amilan CM1023G1000
¥30.50
东丽30%玻纤增强PA6 Amilan CM1011G-30
Amilan CM1011G-30 is a Polyamide 6 (Nylon 6) product filled with 30% glass fiber.
Density(23°C) | 1.36 | -- | g/cm | *** 1183 |
Molding Shrinkage3 | Internal Method | |||
Across Flow : 3.00 mm | 0.50 to 0.80 | -- | % | |
Flow : 3.00 mm | 0.20 to 0.40 | -- | % |
Tensile Stress | *** 527-2 | |||
-40°C | 250 | 225 | MPa | |
23°C | 185 | 105 | MPa | |
80°C | 100 | 70.0 | MPa |
Charpy Notched Impact Strength | *** 179 | |||
-40°C | 10 | 17 | kJ/m | |
23°C | 15 | 23 | kJ/m | |
Charpy Unnotched Impact Strength | *** 179 | |||
-40°C | 70 | 80 | kJ/m | |
23°C | 80 | 100 | kJ/m |
| Thermal | Dry | Conditioned | Unit | Test Method |
Heat Deflection Temperature(0.45 MPa, Unannealed) | 224 | -- | °C | *** 75-2/B |
Melting Temperature | 225 | -- | °C | DSC |
PA6为乳白色或微黄色透明到不透明角质状结晶性聚合物，可自由着色，韧性、***性、自润滑性好、刚性小、耐低温，耐细菌、能慢燃，离火慢熄，有滴落、起泡现象，成型加工性极好：可注塑、吹塑、浇塑、喷涂、粉末成型、机加工、焊接、粘接。PA6 尺寸稳定性差，并影响电性能（击穿电压）。PA6 使用温度可达180℃,加抗冲改性剂后会降至160℃，用15%-50%玻纤增强，可提高至199℃，无机填充PA能提高其热变形温度。