NILAMID B2GF30TF15 PTFE增强PA6
¥36.50
NILAMID B2GF50 50%玻纤PA6
¥29.50
NILAMID B2HHGF50热稳定PA6-GF50
¥29.50
低翘曲PA6 NILAMID B3GB50玻璃珠增强
¥32.50
PA6 NILAMID B3GF15 15%GF
¥27.50
25%玻纤PA6 NILAMID B3GF25
¥26.50
塞拉尼斯V2阻燃PA6 FRIANYL B3V2
Density (23°C) | 1.12 | g/cm³ | ISO 1183 |
Molding Shrinkage | ISO 294-4 | ||
Across Flow : 23°C | 1.6 | % | |
Flow : 23°C | 1.3 | % | |
Water Absorption | ISO 62 | ||
24 hr, 23°C | 2.0 | % | |
Saturation, 23°C | 8.5 | % |
| Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus (23°C) | 3500 | MPa | ISO 527-2 |
Tensile Stress (Yield, 23°C) | 85.0 | MPa | ISO 527-2 |
Tensile Strain (Break, 23°C) | 6.0 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
Charpy Notched Impact Strength | ISO 179/1eA | ||
-30°C | 4.0 | kJ/m² | |
23°C | 4.5 | kJ/m² | |
Charpy Unnotched Impact Strength | ISO 179/1eU | ||
-30°C | No Break | ||
23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
Heat Deflection Temperature | |||
0.45 MPa, Unannealed | 160 | °C | ISO 75-2/B |
1.8 MPa, Unannealed | 65.0 | °C | ISO 75-2/A |
Continuous Use Temperature 3 | 125 | °C | IEC 60216 |
Ball Pressure Test | IEC 60695-10-2 | ||
125°C | Pass | ||
165°C | Pass |
| Electrical | Nominal Value | Unit | Test Method |
Surface Resistivity 4 | 1.0E+13 | ohms | IEC 60093 |
Volume Resistivity (23°C) | 1.0E+15 | ohms·cm | IEC 60093 |
Electric Strength (2.00 mm) | 22 | kV/mm | IEC 60243-1 |
Comparative Tracking Index (3.20 mm, Solution A) | 600 | V | IEC 60112 |
Needle Flame Test | IEC 60695-11-5 | ||
1.00 mm | Pass | ||
2.00 mm | Pass | ||
| Flammability | Nominal Value | Unit | Test Method |
Flame Rating | UL 94 | ||
0.40 mm, NC | V-2 | ||
0.8 mm | V-2 | ||
1.6 mm | V-2 | ||
3.2 mm | V-2 | ||
Glow Wire Flammability Index | IEC 60695-2-12 | ||
0.8 mm | 960 | °C | |
3.2 mm | 960 | °C | |
Oxygen Index | 29 | % | ISO 4589-2 |
PA6工业中的应用
PA6聚酰胺玻纤增强材料可根据产品的特性要求添加玻纤含量在5-60%的范围，这类材料具有很好的强度、耐热性能、优良的抗冲击性能、良好的尺寸稳定性及低翘曲性等。为了满足在工业品方面的使用要求，增强聚酰胺材料应具备以下要求：
1）.优异的强度和耐久性，优良的刚性和耐热性的结合
2）.优异的着色性能，***的表面外观，能够适用于复杂的结构成型，并帮助设计***开发新造型产品
3). 良好的加工性，优异的流动性及热稳定性使材料加工条件更为宽松，使注塑件微型化
4). 极高的热稳定性，能在高达270度的波峰焊锡中不挂锡
在线问