泰科纳OMNILON PA6 GR55 55%GF增强PA6
| ISO | Value | Unit | Test Standard |
| Density | 1620 | kg/m | ISO 1183 |
| Tensile stress at yield, 23°C | 234 | MPa | ASTM D 638 |
| Tensile strain at break, 23°C | 3 | % | ASTM D 638 |
| Flexural modulus, 23°C | 17200 | MPa | ASTM D 790 |
| Flexural stress, 23°C | 331 | MPa | ASTM D 790 |
| Izod impact notched, 23°C | 139 | J/m | ASTM D 256 |
| DTUL at 1.8 MPa | 213 | °C | ISO 75-1, -2 |
| DTUL at 0.45 MPa | 218 | °C | ISO 75-1, -2 |
| Pre Drying | Value | Unit | Test Standard |
| Necessary low maximum residual moisture content | 0.15 | % | - |
| Drying time | 4 - 8 | h | - |
| Drying temperature | 80 - 90 | °C | - |
| Temperature | Value | Unit | Test Standard |
| Zone1 temperature | 220 - 230 | °C | - |
| Zone2 temperature | 225 - 235 | °C | - |
| Zone3 temperature | 235 - 245 | °C | - |
| Zone4 temperature | 245 - 255 | °C | - |
| Nozzle temperature | 255 - 270 | °C | - |
| Melt temperature | 250 - 270 | °C | - |
| Mold temperature | 60 - 80 | °C | - |
| Hot runner temperature | 255 - 270 | °C | - |
PA6日常用品中的应用
PA6玻纤增强材料具有良好的尺寸稳定性及低翘曲性、焊锡性及烤漆性、易喷涂、可过超声波焊接、材料光泽度好，可染成各种鲜艳的颜色，为了满足在工业品方面的使用要求，增强PA6材料应具备以下要求：
1). 强度和耐久性，优良的刚性和耐热性的结合
2). 优化部件设计，***的着色性能，***的表面外观，能够适用于复杂的结构成型，并帮助设计***开发新造型产品
3). 良好的加工性，***的流动性及热稳定性使材料加工条件更为宽松，使注塑件微型化
4). 极高的热稳定性，能在高达270度的波峰焊锡中不挂锡
5). ***的温度和频率范围内恒定的电气性，确保装置设备的使用***百安全