原包德国朗盛低翘曲PA6 Durethan BG30FN05玻璃珠30%
| C | Molding shrinkage, parallel | 60x60x2; 260 °C / MT 80 °C; 600 bar | % | *** 294-4 | 0,8 | |
| C | Molding shrinkage, transverse | 60x60x2; 260 °C / MT 80 °C; 600 bar | % | *** 294-4 | 0,8 | |
| Post- shrinkage, parallel | 60x60x2; 120 °C; 4 h | % | *** 294-4 | 0.2 | ||
| Post- shrinkage, transverse | 60x60x2; 120 °C; 4 h | % | *** 294-4 | 0.2 | ||
Mechanical properties (23 °C/50 % r. h.) | ||||||
| C | Tensile modulus | 1 mm/min | MPa | *** 527-1,-2 | 5400 | 2100 |
| C | Tensile Stress at break | 5 mm/min | MPa | *** 527-1,-2 | 75 | 30 |
| C | Tensile Strain at break | 5 mm/min | % | *** 527-1,-2 | 2.2 | >20 |
| C | Charpy impact strength | 23 °C | kJ/m | *** 179-1eU | 40 | 60 |
| C | Charpy impact strength | -30 °C | kJ/m | *** 179-1eU | 38 | 25 |
| C | Charpy notched impact strength | 23 °C | kJ/m | *** 179-1eA | <10 | <10 |
| C | Charpy notched impact strength | -30 °C | kJ/m | *** 179-1eA | <10 | <10 |
| Izod impact strength | 23 °C | kJ/m | *** 180-1U | 30 | 45 | |
| Izod impact strength | -30 °C | kJ/m | *** 180-1U | 30 | 20 | |
| Izod notched impact strength | 23 °C | kJ/m | *** 180-1A | <10 | <10 | |
| Izod notched impact strength | -30 °C | kJ/m | *** 180-1A | <10 | <10 | |
| C | Burning behavior UL 94 | 1.5 mm | Class | UL 94 | V-0 | |
| C | Burning behavior UL 94 | 0.4 mm | Class | UL 94 | V-0 | |
| Burning behavior UL 94 | 0.75 mm | Class | UL 94 | V-0 | ||
| Burning behavior UL 94 | 3.0 mm | Class | UL 94 | V-0 |