食品级PA6 Ultramid B3S FC R01
¥29.50
PA6 Ultramid B3S HP高流动
¥28.50
原包巴斯夫高流动PA6 Ultramid B3S阻燃V2
Density / Specific Gravity | 1.13 | g/cm³ | ASTM D792, ISO 1183 |
Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 150 | cm³/10min | ISO 1133 |
Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus (23°C) | 3200 | MPa | ISO 527-2 |
Tensile Strength | |||
Yield, 23°C | 79.0 | MPa | ASTM D638 |
Yield, 23°C | 85.0 | MPa | ISO 527-2 |
Tensile Strain | |||
Yield, 23°C | 3.8 | % | ISO 527-2 |
Break, 23°C | 4.2 | % | ASTM D638 |
Flexural Modulus (23°C) | 2740 | MPa | ASTM D790 |
Impact | Nominal Value | Unit | Test Method |
Charpy Notched Impact Strength (23°C) | 3.0 | kJ/m² | ISO 179 |
Notched Izod Impact | |||
23°C | 53 | J/m | ASTM D256 |
23°C | 5.0 | kJ/m² | ISO 180 |
Flame Rating | UL 94 | ||
0.75 mm | V-2 | ||
1.5 mm | V-2 | ||
3.0 mm | V-2 |
原包巴斯夫高流动PA6 Ultramid B3S阻燃V2