Density (23°C) | 1.31 | -- | g/cm³ | ISO 1183 |
Molding Shrinkage | ISO 294-4 | |||
Across Flow : 120°C, 2.00 mm 3 | 0.10 | -- | % | |
Across Flow : 260°C, 2.00 mm 4 | 0.70 | -- | % | |
Flow : 120°C, 2.00 mm 3 | 0.10 | -- | % | |
Flow : 260°C, 2.00 mm 4 | 0.60 | -- | % | |
Water Absorption | ISO 62 | |||
Saturation, 23°C | 7.0 | -- | % | |
Equilibrium, 23°C, 50% RH | 2.1 | -- | % |
Mechanical | Dry | Conditioned | Unit | Test Method |
Tensile Modulus (23°C) | 6100 | 3100 | MPa | ISO 527-2/1 |
Tensile Stress (Break, 23°C) | 100 | 55.0 | MPa | ISO 527-2/5 |
Tensile Strain (Break, 23°C) | 3.0 | 15 | % | ISO 527-2/5 |
Flexural Modulus 5 (23°C) | 6100 | 3200 | MPa | ISO 178/A |
Flexural Stress 5 | ISO 178/A | |||
23°C | 170 | 90.0 | MPa | |
3.5% Strain, 23°C | 165 | 75.0 | MPa | |
Flexural Strain at Flexural Strength 6 (23°C) | 4.5 | 7.0 | % | ISO 178/A |
Impact | Dry | Conditioned | Unit | Test Method |
Charpy Notched Impact Strength | ISO 179/1eA | |||
-30°C | <10 | <10 | kJ/m² | |
23°C | <10 | <10 | kJ/m² | |
Charpy Unnotched Impact Strength | ISO 179/1eU | |||
-30°C | 30 | -- | kJ/m² | |
23°C | 35 | 100 | kJ/m² |
Heat Deflection Temperature | ||||
0.45 MPa, Unannealed | 215 | -- | °C | ISO 75-2/B |
1.8 MPa, Unannealed | 185 | -- | °C | ISO 75-2/A |
直销朗盛PA6 Durethan BKV20FN20无卤阻燃20%GF