30%玻纤无卤高光PA6 SCHULAMID 6 GF 30 4DD BLACK
Density | 1.43 | -- | g/cm | ISO 1183/A |
Viscosity Number | 145 | -- | cm/g | ISO 307 |
Mechanical | Dry | Conditioned | Unit | Test Method |
Tensile Modulus | 12000 | 6500 | MPa | ISO 527-1/1A/1 |
Tensile Stress(Break) | 140 | 95.0 | MPa | ISO 527-2/1A/5 |
Tensile Strain(Break) | 3.0 | 6.0 | % | ISO 527-2/1A/5 |
Impact | Dry | Conditioned | Unit | Test Method |
Charpy Notched Impact Strength | ISO 179/1eA | |||
-30°C | 9.0 | -- | kJ/m | |
23°C | 12 | 16 | kJ/m | |
Charpy Unnotched Impact Strength | ISO 179/1eU | |||
-30°C | 60 | -- | kJ/m | |
23°C | 70 | 70 | kJ/m |
Thermal | Dry | Conditioned | Unit | Test Method |
Deflection Temperature Under Load | ||||
0.45 MPa, Unannealed | 215 | -- | °C | ISO 75-2/Bf |
1.8 MPa, Unannealed | 204 | -- | °C | ISO 75-2/Af |
Vicat Softening Temperature | ||||
-- | 203 | -- | °C | ISO 306/B50 |
-- | 212 | -- | °C | ISO 306/A50 |
Ball Pressure Test(200°C) | Pass | -- | IEC 60695-10-2 |
Electrical | Dry | Conditioned | Unit | Test Method |
Surface Resistivity | > 1.0E+15 | > 1.0E+12 | ohms | IEC 60093 |
Volume Resistivity | > 1.0E+13 | > 1.0E+10 | ohms·m | IEC 62631-3-1 |
Electric Strength2(23°C, 1.00 mm, in Oil) | 28 | -- | kV/mm | IEC 60243-1 |
Comparative Tracking Index | 475 | -- | V | IEC 60112 |
Flammability | Dry | Conditioned | Unit | Test Method |
Burning Rate | ISO 3795 | |||
0.750 mm, Self-Extinguishing | 0.0 | -- | mm/min | |
1.50 mm, Self-Extinguishing | 0.0 | -- | mm/min | |
3.00 mm, Self-Extinguishing | 0.0 | -- | mm/min | |
Flammability Classification | IEC 60695-11-10, -20 | |||
0.75 mm | V-0 | -- | ||
1.5 mm | V-0 | -- | ||
3.0 mm | V-0 | -- |