矿物增强PA66 Vydyne R220
¥38.50
玻矿低翘曲PA66 Vydyne R860
¥37.50
抗冲击PA66 Vydyne 41 NT
¥41.50
***冲击PA66 Vydyne 41H
¥44.50
增韧耐寒PA66 Vydyne 47
¥46.50
奥升德（首诺）过960度灼热丝PA66 Vydyne FR350J
Density | 1.31 | g/cm | *** 1183 |
Molding Shrinkage | *** 294-4 | ||
Across Flow : 23°C, 2.00 mm | 1.7 | % | |
Flow : 23°C, 2.00 mm | 1.4 | % | |
Water Absorption | *** 62 | ||
24 hr, 23°C | 0.80 | % | |
Equilibrium, 23°C, 50% RH | 1.9 | % |
| Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus(23°C) | 3200 | MPa | *** 527-2 |
Tensile Stress(Break, 23°C) | 70.0 | MPa | *** 527-2 |
Tensile Strain(Break, 23°C) | 15 | % | *** 527-2 |
Flexural Modulus(23°C) | 3200 | MPa | *** 178 |
Flexural Strength(23°C) | 90.0 | MPa | *** 178 |
Poisson&＃39;s Ratio | 0.40 | *** 527-2 | |
| Impact | Nominal Value | Unit | Test Method |
Charpy Notched Impact Strength(23°C) | 4.3 | kJ/m | *** 179/1eA |
Charpy Unnotched Impact Strength(23°C) | 65 | kJ/m | *** 179/1eU |
Notched Izod Impact Strength(23°C) | 4.1 | kJ/m | *** 180 |
Heat Deflection Temperature(1.8 MPa, Unannealed) | 75.0 | °C | *** 75-2/A |
Melting Temperature | 265 | °C | *** 11357-3 |
Flame Rating | UL 94 | ||
0.40 mm | V-0 | ||
0.75 mm | V-0 | ||
1.5 mm |
|
PA66 聚酰胺66或尼龙66化学和物理特性PA66在聚酰胺材料中有较高的熔点。它是一种半晶体-晶体材料。PA66在较高温度也能保持较强的强度和刚度。在产品设计时，一定要考虑吸湿性对几何稳定性的影响。为了提高PA66的机械特性，经常加入各种各样的改性剂。玻璃就是***常见的添加剂，有时为了提高抗冲击性还加入合成橡胶，如EPDM和SBR等。 PA66的粘性较低，因此流动性很好（但不如PA6）。
在线问