热稳定PA66 TECHNYL A 216T V33索尔维33%玻纤
Density | 1.40 | -- | g/cm | *** 1183/A |
Molding Shrinkage | *** 294-4 | |||
Across Flow | 1.1 | -- | % | |
Flow | 0.30 | -- | % | |
Water Absorption | *** 62 | |||
24 hr, 23°C | 0.78 | -- | % | |
Equilibrium, 23°C, 50% RH | 1.9 | -- | % |
Mechanical | Dry | Conditioned | Unit | Test Method |
Tensile Modulus(23°C) | 11000 | 8300 | MPa | *** 527-2/1A |
Tensile Stress(Break, 23°C) | 200 | 145 | MPa | *** 527-2/1A |
Tensile Strain(Break, 23°C) | 2.8 | 4.3 | % | *** 527-2 |
Flexural Modulus | ||||
23°C | 10600 | -- | MPa | ASTM D790 |
23°C | 9200 | 6400 | MPa | *** 178 |
Flexural Strength | ||||
23°C | 270 | -- | MPa | ASTM D790 |
23°C | 190 | -- | MPa | *** 178 |
Impact | Dry | Conditioned | Unit | Test Method |
Charpy Notched Impact Strength(23°C) | 13 | 17 | kJ/m | *** 179/1eA |
Charpy Unnotched Impact Strength(23°C) | 70 | 78 | kJ/m | *** 179/1eU |
Notched Izod Impact | ||||
23°C | 98 | -- | J/m | ASTM D256 |
23°C | 12 | 17 | kJ/m | *** 180 |
Unnotched Izod Impact Strength(23°C) | 65 | -- | kJ/m | *** 180/1U |
Thermal | Dry | Conditioned | Unit | Test Method |
Deflection Temperature Under Load | ||||
1.8 MPa, Unannealed | 250 | -- | °C | ASTM D648 |
1.8 MPa, Unannealed | 255 | -- | °C | *** 75-2/Af |
Melting Temperature | 263 | -- | °C | *** 11357-3 |
PA66优点
1、具高抗张强度;2、耐韧、耐冲击性特优;3、自润性、***性佳;4、低温特性佳;5、具自熄性;
PA66用途
***应用于机械、仪器仪表、汽车部件、电子电气、铁路、家电、通讯、纺机、体育休闲用品、油管、油箱及一些***工程制品。
电子电器:连接器、卷线轴、计时器、护盖断路器、开关壳座
汽车: 散热风扇、门把、油箱盖、进气隔栅、水箱护盖、灯座
工业零件:椅座、自行车输框、溜冰鞋底座、纺织梭、踏板、滑输