热稳定25%GF增强PA66 TECHNYL AR218V25索尔维
Density | 1.32 | -- | g/cm | *** 1183/A |
Water Absorption | *** 62 | |||
24 hr, 23°C | 0.90 | -- | % | |
Saturation, 23°C | 6.2 | -- | % | |
Equilibrium, 23°C, 50% RH | 2.3 | -- | % |
Mechanical | Dry | Conditioned | Unit | Test Method |
Tensile Modulus(23°C) | 7800 | 5000 | MPa | *** 527-2/1A |
Tensile Stress(Break, 23°C) | 125 | 95.0 | MPa | *** 527-2/1A |
Tensile Strain(Break, 23°C) | 2.5 | 10 | % | *** 527-2 |
Flexural Modulus(23°C) | 7200 | -- | MPa | *** 178 |
Flexural Stress(23°C) | 200 | -- | MPa | *** 178 |
Impact | Dry | Conditioned | Unit | Test Method |
Charpy Notched Impact Strength(23°C) | 5.0 | -- | kJ/m | *** 179/1eA |
Charpy Unnotched Impact Strength(23°C) | 40 | -- | kJ/m | *** 179/1eU |
Notched Izod Impact Strength(23°C) | 5.5 | -- | kJ/m | *** 180 |
Thermal | Dry | Conditioned | Unit | Test Method |
Heat Deflection Temperature(1.8 MPa, Unannealed) | 240 | -- | °C | *** 75-2/Af |
Melting Temperature | 260 | -- | °C | *** 11357-3 |
Flammability | Dry | Conditioned | Test Method | |
Flame Rating(1.6 mm) | HB | -- | UL 94 |