巴斯夫25%GF阻燃PA66 ULTRAMID EMG5FR

Mechanicalproperty	Value	Unit	Method	Condition

Flexural modulus	9806.8	MPa	ASTM D790	Dry
Izod impact strength(ASTM), Notched	8.0	J/m	ASTM D256	23℃, Dry
Flexural strength at break	215.75	MPa	ASTM D790	Dry
Tensile strength at yield	142.2	MPa	ASTM D638	Dry
Elongation at break	2.4	%	ASTM D638	Dry
Physicalproperty	Value	Unit	Method	Condition
Density	1.68	g/	ASTM D792	Dry
Thermalproperty	Value	Unit	Method	Condition
Heat Deflection Temperature	247.0	C	ASTM D648	Dry
Flammabilityproperty	Value	Unit	Method	Condition
Flammability	V-0	class	UL94	0.88mm
Otherproperty	Value	Unit	Method	Condition
Mold shrinkage	0.03 ~ 0.07	%	ASTM D955	Dry, Bar 2×60×60mm
Mold temp	260.0 ~ 300.0	C
Drying temperature	100.0 ~ 120.0	C		3~5hr
Metallic pattern temperature	82.0	C

PA66（聚酰胺66或尼龙66），同PA6相比，PA66更***应用于汽车工业、仪器壳体以及其它需要有抗冲击性和高强度要求的产品。***用于制造机械、汽车、化学与电气装置的零件，如齿轮、滚子、滑轮、辊轴、泵体中叶轮、风扇叶片、高压密封围、阀座、垫片、衬套、各种把手、支撑架、电线包内层等。

PA66塑胶原料为半透明或不透明乳白包或带黄色颗粒状结晶形聚合物，具有可塑性。密度（g/cm3） 1．10-1．14；拉伸强度(MPa) 60. 0-80．0；洛氏硬度118；熔点252℃；脆化温度-30℃；热分解温度大于350℃；连续耐热80-120℃；冲击强度（kJ/m2） 60-100；静弯曲强度(MPa) 1 00-120；马丁耐热(℃) 50-60；弯曲弹性模量 (MPa) 2000～3000；体积电阻率（Ωcm） 1.83×1015；平衡吸水率2．5%；介电常数 1．63。