PA66 ZYTEL 70G50HSL热稳定50%玻纤
¥35.50
20%芳纶增强PA66 ZYTEL 70K20HSL
¥65.50
PA66 ZYTEL 79G13L玻纤增强13%
¥35.50
14%GF热稳定PA66 ZYTEL 8018HS
¥35.50
原包美国杜邦43%玻纤PA66 ZYTEL 70G43L
Density | 1.49 | -- | g/cm | *** 1183 |
Molding Shrinkage | *** 294-4 | |||
Across Flow | 1.0 | -- | % | |
Flow | 0.30 | -- | % | |
Water Absorption | *** 62 | |||
24 hr, 23°C, 2.00 mm | 0.90 | -- | % | |
Saturation, 23°C, 2.00 mm | 4.7 | -- | % | |
Equilibrium, 23°C, 2.00 mm, 50% RH | 1.5 | -- | % | |
| Hardness | Dry | Conditioned | Unit | Test Method |
Rockwell Hardness | *** 2039-2 | |||
M-Scale | 105 | 90 | ||
R-Scale | 125 | 118 | ||
Ball Indentation Hardness(H 961/30) | 290 | -- | MPa | *** 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
Tensile Modulus | 14000 | 11000 | MPa | *** 527-2 |
Tensile Stress(Break) | 225 | 160 | MPa | *** 527-2 |
Tensile Strain(Break) | 3.0 | 4.0 | % | *** 527-2 |
Tensile Creep Modulus | *** 899-1 | |||
1 hr | -- | 10800 | MPa | |
1000 hr | -- | 7960 | MPa | |
Flexural Modulus | 12000 | 9000 | MPa | *** 178 |
Flexural Stress | 340 | 260 | MPa | *** 178 |
Poisson&＃39;s Ratio | 0.33 | 0.34 | ||
| Impact | Dry | Conditioned | Unit | Test Method |
Charpy Notched Impact Strength | *** 179/1eA | |||
-40°C | 11 | 11 | kJ/m | |
-30°C | 12 | 12 | kJ/m | |
23°C | 16 | 19 | kJ/m |
Flame Rating | UL 94,IEC 60695-11-10, -20 | |||
0.71 mm | HB | -- | ||
1.5 mm | HB | -- |