代理朗盛PA66 Durethan AKV25FN04无卤阻燃25%GF
Density(23°C) | 1.38 | -- | g/cm | ISO 1183 |
Molding Shrinkage | ISO 294-4 | |||
Across Flow : 120°C, 2.00 mm3 | 0.10 | -- | % | |
Across Flow : 270°C, 2.00 mm4 | 1.0 | -- | % | |
Flow : 120°C, 2.00 mm5 | 0.10 | -- | % | |
Flow : 270°C, 2.00 mm4 | 0.50 | -- | % | |
Water Absorption | ISO 62 | |||
Saturation, 23°C | 4.8 | -- | % | |
Equilibrium, 23°C, 50% RH | 1.6 | -- | % |
Mechanical | Dry | Conditioned | Unit | Test Method |
Tensile Modulus(23°C) | 9300 | 5700 | MPa | ISO 527-2/1 |
Tensile Stress(Break, 23°C) | 120 | 80.0 | MPa | ISO 527-2/5 |
Tensile Strain(Break, 23°C) | 3.3 | 6.5 | % | ISO 527-2/5 |
Flexural Modulus6(23°C) | 8900 | 5700 | MPa | ISO 178/A |
Flexural Stress6 | ISO 178/A | |||
23°C | 200 | 135 | MPa | |
3.5% Strain, 23°C | -- | 120 | MPa | |
Flexural Strain at Flexural Strength7(23°C) | 3.4 | 6.0 | % | ISO 178/A |
Impact | Dry | Conditioned | Unit | Test Method |
Charpy Notched Impact Strength | ISO 179/1eA | |||
-30°C | <10 | <10 | kJ/m | |
23°C | <10 | 13 | kJ/m | |
Charpy Unnotched Impact Strength | ISO 179/1eU | |||
-30°C | 60 | 55 | kJ/m | |
23°C | 60 | 65 | kJ/m | |
Notched Izod Impact Strength(23°C) | <10 | -- | kJ/m | ISO 180/1A |
Unnotched Izod Impact Strength(23°C) | 50 | 60 | kJ/m | ISO 180/1U |
Flame Rating | UL 94 | |||
0.40 mm | V-0 | -- | ||
1.5 mm |
| -- |
代理朗盛PA66 Durethan AKV25FN04无卤阻燃25%GF