35% Glass Reinforced Heat Stabilized Polyamide 66 Zytel 70G35HSLX BK357 is a 35% glass fiber reinforced heat stabilized black polyamide 66 for injection molding.
物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
密度 | 1.24 g/cc | 0.0448 lb/in³ | |
1.41 g/cc | 0.0509 lb/in³ | DAM; ISO 1183 | |
吸水率 | 5.5 % @Thickness 2.00 mm | 5.5 % @Thickness 0.0787 in | DAM; Sim. to ISO 62 |
水分吸收 | 1.70 % @Thickness 2.00 mm | 1.70 % @Thickness 0.0787 in | DAM; Sim. to ISO 62 |
粘度 | 58900 cP @Shear Rate 5000 1/s, Temperature 305 °C | 58900 cP @Shear Rate 5000 1/s, Temperature 581 °F | ISO 11403-1 -2 |
70480 cP @Shear Rate 5000 1/s, Temperature 295 °C | 70480 cP @Shear Rate 5000 1/s, Temperature 563 °F | ISO 11403-1 -2 | |
85520 cP @Shear Rate 5000 1/s, Temperature 285 °C | 85520 cP @Shear Rate 5000 1/s, Temperature 545 °F | ISO 11403-1 -2 | |
179600 cP @Shear Rate 500 1/s, Temperature 305 °C | 179600 cP @Shear Rate 500 1/s, Temperature 581 °F | ISO 11403-1 -2 | |
226700 cP @Shear Rate 500 1/s, Temperature 295 °C | 226700 cP @Shear Rate 500 1/s, Temperature 563 °F | ISO 11403-1 -2 | |
287300 cP @Shear Rate 500 1/s, Temperature 285 °C | 287300 cP @Shear Rate 500 1/s, Temperature 545 °F | ISO 11403-1 -2 | |
粘度测试 | 145 cm³/g | 145 cm³/g | DAM; ISO 307 1157 1628 |
线性成型收缩率,Flow | 0.0030 cm/cm | 0.0030 in/in | DAM; ISO 294-4 2577 |
线性成型收缩率,横向 | 0.011 cm/cm | 0.011 in/in | DAM; ISO 294-4 2577 |