经销德国巴斯夫PA66 ULTRAMID A3WG5耐热25%玻纤增强PA66
Density / Specific Gravity | 1.32 | -- | g/cm³ | ASTM D792, ISO 1183 |
Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 50 | -- | cm³/10min | ISO 1133 |
Molding Shrinkage - Flow (3.18 mm) | 0.30 | -- | % | |
Water Absorption | ||||
Saturation | 6.0 | -- | % | ASTM D570 |
Saturation, 23°C | 6.0 | -- | % | ISO 62 |
Equilibrium, 50% RH | 1.9 | -- | % | ASTM D570 |
Equilibrium, 23°C, 50% RH | 1.9 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
Tensile Modulus (23°C) | 8600 | 6500 | MPa | ISO 527-1 |
Tensile Strength | ||||
Break, 23°C | 169 | 118 | MPa | ASTM D638 |
Break, 23°C | 180 | 120 | MPa | ISO 527-2 |
Tensile Elongation | ||||
Break, 23°C | 2.8 | 5.0 | % | ASTM D638 |
Break, 23°C | 2.8 | 6.0 | % | ISO 527-2 |
Flexural Modulus | ||||
23°C | 7720 | 5380 | MPa | ASTM D790 |
23°C | 7600 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
Charpy Notched Impact Strength | ISO 179 | |||
-30°C | 9.0 | -- | kJ/m² | |
23°C | 10 | 20 | kJ/m² | |
Charpy Unnotched Impact Strength | ISO 179 | |||
-30°C | 55 | -- | kJ/m² | |
23°C | 60 | 90 | kJ/m² | |
Notched Izod Impact | ||||
-40°C | 69 | -- | J/m | ASTM D256 |
23°C | 80 | -- | J/m | ASTM D256 |
23°C | 9.5 | -- | kJ/m² | ISO 180 |
为您推荐
-
PA6 B3EG10高刚50%玻纤增强PA6 ¥34.00
-
PA6 B3EG3高抗冲15%GF耐油PA6 ¥34.00
-
PA6 B3EG4耐油20%玻纤增强PA6 ¥33.00
-
PA6 ULTRAMID B3EG5高强度25%玻纤增强 ¥32.00
-
PA6 ULTRAMID B3EG6高刚级30%GF增强 ¥34.00
-
在线问
产品参数
- 耐热PA66
- 否
- 德国
- 德国巴斯夫
- A3WG5
- 品牌经销
- 标准料
- PA66
- 注塑级
- 增强级、 耐高温、 耐老化、 高强度、 高刚性
- 汽车部件、 电子电器部件、 家电部件、 电动工具配件
- ULTRAMID
- 25KG/包