热稳定40%玻璃珠PA66 Bergamid A70 G/GK40 H
Density | 1.45 | g/cm³ | ISO 1183 |
Melt Mass-Flow Rate (MFR) (275°C/2.16 kg) | 15 | g/10 min | ISO 1133 |
Melt Volume-Flow Rate (MVR) (275°C/2.16 kg) | 12 | cm³/10min | ISO 1133 |
Molding Shrinkage | 0.63 | % | ISO 294-4 |
Viscosity Number | 140 | cm³/g | ISO 307 |
Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus (23°C) | 6000 | MPa | ISO 527-1/1 |
Tensile Stress (Break, 23°C) | 120 | MPa | ISO 527-2 |
Tensile Strain (Break, 23°C) | 2.5 | % | ISO 527-2 |
Flexural Modulus | 6200 | MPa | ISO 178 |
Flexural Stress | 180 | MPa | ISO 178 |
Impact | Nominal Value | Unit | Test Method |
Charpy Notched Impact Strength (23°C) | 6.0 | kJ/m² | ISO 179 |
Charpy Unnotched Impact Strength (23°C) | 25 | kJ/m² | ISO 179 |
Thermal | Nominal Value | Unit | Test Method |
Deflection Temperature Under Load (1.8 MPa, Unannealed) | 230 | °C | ISO 75-2/A |
Electrical | Nominal Value | Unit | Test Method |
Surface Resistivity | 1.0E+13 | ohms | IEC 60093 |
Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
Comparative Tracking Index (Solution A) | 500 | V | IEC 60112 |