LG Chemical AF360 ABS, TBBA-free Flame Retardant 物性表
物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
比重 | 1.19 g/cc | 1.19 g/cc | ASTM D792 |
处理 | 0.010 | 0.010 | Injection Molding |
线性成型收缩率,Flow | 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm | 0.0040 - 0.0070 in/in @Thickness 0.126 in | ASTM D955 |
熔体流动速率 | 26 g/10 min @Load 10.0 kg, Temperature 220 °C | 26 g/10 min @Load 22.0 lb, Temperature 428 °F | ASTM D1238 |
机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
洛氏硬度(R 级) | 98 | 98 | ASTM D785 |
抗张强度(屈服) | 36.3 MPa @Thickness 3.20 mm | 5260 psi @Thickness 0.126 in | 50 mm/min; ASTM D638 |
伸长率 (断裂) | 20 % @Thickness 3.20 mm | 20 % @Thickness 0.126 in | 50 mm/min; ASTM D638 |
屈服伸长率 | >= 5.0 % @Thickness 3.20 mm | >= 5.0 % @Thickness 0.126 in | 50 mm/min; ASTM D638 |
拉伸模量 | 2.06 GPa @Thickness 3.20 mm | 299 ksi @Thickness 0.126 in | 1 mm/min; ASTM D638 |
弯曲强度 | 60.8 MPa @Thickness 6.40 mm | 8820 psi @Thickness 0.252 in | 15 mm/min; ASTM D790 |
弯曲模量 | 2.26 GPa @Thickness 6.40 mm | 327 ksi @Thickness 0.252 in | 15 mm/min; ASTM D790 |
悬壁梁缺口冲击强度 | 1.47 J/cm @Thickness 6.40 mm, Temperature 23.0 °C | 2.76 ft-lb/in @Thickness 0.252 in, Temperature 73.4 °F | ASTM D256 |