食品级PBT Crastin FG6129
¥28.50
食品级PBT Crastin FG6130
¥28.50
增韧抗冲PBT Crastin ST820
¥28.50
阻燃PBT Crastin HTI668FR
¥28.50
阻燃低翘曲PBT Crastin LW9020FR
¥28.50
30%玻纤阻燃PBT Crastin LW9030FR
¥28.50
注塑级PBT Crastin 6130C
| 收缩率 | ASTM D955 | ||
| (平行流动方向) | 0.016 | cm/cm | |
| (垂直流动方向) | 0.016 | cm/cm |
| 机械性能 | 额定值 | 单位 | 测试方法 |
|---|---|---|---|
| 弯曲模量 | ASTM D790 | ||
| (90 °C, 0.00 mm, Injection Molded, Procedure A, Method I (3 point load), 0.00 mm, Type I, Secant) | 331 | Mpa | |
| ((-40 °C, 0.00 mm, Injection Molded, Procedure A, Method I (3 point load), 0.00 mm, Type I, Secant) | 3000 | Mpa | |
| (23 °C, 0.00 mm, Injection Molded, Procedure A, Method I (3 point load), 0.00 mm, Type I, Secant) | 2410 | Mpa | |
| (149 °C, 0.00 mm, Injection Molded, Procedure A, Method I (3 point load), 0.00 mm, Type I, Secant) | 234 | Mpa | |
| 弯曲强度 | ASTM D790 | ||
| (90 °C, 0.00 mm, Injection Molded, Method I (3 point load), Procedure A, 0.00 mm, Type I) | 13 | Mpa | |
| ((-40 °C, 0.00 mm, Injection Molded, Method I (3 point load), Procedure A, 0.00 mm, Type I) | 120 | Mpa | |
| (23 °C, 0.00 mm, Injection Molded, Method I (3 point load), Procedure A, 0.00 mm, Type I) | 80 | Mpa | |
| (149 °C, 0.00 mm, Injection Molded, Method I (3 point load), Procedure A, 0.00 mm, Type I) | 8 | Mpa | |
| 断裂点伸长率 | ASTM D638 | ||
| (90 °C, 0.00 mm, Compression Molded, Type I) | 300 | % | |
| (-40 °C, 0.00 mm, Compression Molded, Type I) | 11 | % | |
| (23 °C, 0.00 mm, Compression Molded, Type I) | 300 | % | |
| (150 °C, 0.00 mm, Compression Molded, Type I) | 300 | % | |
| 非缺口冲击强度 | ASTM D256 | ||
| (-40 °C, 0.00 mm) | No Break | J/m | |
| (23 °C, 0.00 mm) | No Break | J/m |
| 热性能 | 额定值 | 单位 | 测试方法 |
|---|---|---|---|
| 熔点 | 225 | ℃ | DSC |
| 阻燃性 | UL94 | ||
| (3.00 mm) | HB | ||
| (1.5mm) | HB | ||
| (0.81mm) | HB |
在线问