| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.31 g/cc | 1.31 g/cc | ASTM D792 |
| Density | 1.31 g/cc | 0.0473 lb/in³ | *** 1183 |
| Filler Content | 15 % | 15 % | ASTM D229 |
| Water Absorption | 0.80 % | 0.80 % | 23°C/sat; *** 62 |
| Moisture Absorption | 0.300 % | 0.300 % | 23°C / 50% RH; *** 62 |
| Viscosity | 155 cP @Shear Rate 1500 1/s, Temperature 260 °C | 155 cP @Shear Rate 1500 1/s, Temperature 500 °F | melt; *** 11443 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0060 cm/cm | 0.0020 - 0.0060 in/in | SABIC method |
| Linear Mold Shrinkage, Transverse | 0.0030 - 0.0070 cm/cm | 0.0030 - 0.0070 in/in | SABIC method |
| Melt Flow | 20 g/10 min @Load 5.00 kg, Temperature 250 °C | 20 g/10 min @Load 11.0 lb, Temperature 482 °F | cm³/10 min; *** 1133 |
| 30 g/10 min @Load 5.00 kg, Temperature 265 °C | 30 g/10 min @Load 11.0 lb, Temperature 509 °F | cm³/10 min; *** 1133 | |
| 33 g/10 min @Load 5.00 kg, Temperature 265 °C | 33 g/10 min @Load 11.0 lb, Temperature 509 °F | ASTM D1238 | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 120 | 120 | *** 2039-2 |
| Ball Indentation Hardness | 100 MPa | 14500 psi | *** 2039-1 |
| Tensile Strength at Break | 80.0 MPa | 11600 psi | 5 mm/min; *** 527 |
| 85.0 MPa | 12300 psi | 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 80.0 MPa | 11600 psi | 5 mm/min; *** 527 |
| 85.0 MPa | 12300 psi | 5 mm/min; ASTM D638 | |
| Elongation at Break | 3.0 % | 3.0 % | 5 mm/min; ASTM D638 |
| 4.0 % | 4.0 % | 5 mm/min; *** 527 | |
| Elongation at Yield | 3.0 % | 3.0 % | 5 mm/min; ASTM D638 |
| 4.0 % | 4.0 % | 5 mm/min; *** 527 | |
| Tensile Modulus | 5.60 GPa | 812 ksi | 5 mm/min; ASTM D638 |
| 5.70 GPa | 827 ksi | 1mm/min; *** 527 | |
| Flexural Strength | 125 MPa | 18100 psi | brk, 1.3 mm/min, 50 mm span; ASTM D790 |
| 130 MPa | 18900 psi | 2 mm/min; break; *** 178 | |
| Flexural Yield Strength | 125 MPa | 18100 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 130 MPa | 18900 psi | 2 mm/min; *** 178 | |
| Flexural Modulus | 4.20 GPa | 609 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 4.60 GPa | 667 ksi | 2 mm/min; *** 178 | |
| Flexural Strain at Break | 4.0 % | 4.0 % | 2 mm/min; *** 178 |
| Izod Impact, Notched | 0.650 J/cm | 1.22 ft-lb/in | ASTM D256 |
| 0.500 J/cm @Temperature -30.0 °C | 0.937 ft-lb/in @Temperature -22.0 °F | ASTM D256 | |
| 0.600 J/cm @Temperature 0.000 °C | 1.12 ft-lb/in @Temperature 32.0 °F | ASTM D256 | |
| Izod Impact, Unnotched | 5.20 J/cm | 9.74 ft-lb/in | ASTM D4812 |
| 4.90 J/cm @Temperature -30.0 °C | 9.18 ft-lb/in @Temperature -22.0 °F | ASTM D4812 | |
| Izod Impact, Notched (***) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; *** 180/1A |
| 5.00 kJ/m² @Temperature -30.0 °C | 2.38 ft-lb/in² @Temperature -22.0 °F | 80*10*4; *** 180/1A | |
| 6.00 kJ/m² @Temperature 0.000 °C | 2.86 ft-lb/in² @Temperature 32.0 °F | 80*10*4; *** 180/1A | |
| Izod Impact, Unnotched (***) | 35.0 kJ/m² | 16.7 ft-lb/in² | 80*10*4; *** 180/1U |
| 25.0 kJ/m² @Temperature -30.0 °C | 11.9 ft-lb/in² @Temperature -22.0 °F | 80*10*4; *** 180/1U | |
| Charpy Impact Unnotched | 4.50 J/cm² | 21.4 ft-lb/in² | *** 179/2C |
| 3.00 J/cm² @Temperature -30.0 °C | 14.3 ft-lb/in² @Temperature -22.0 °F | *** 179/2C | |
| Charpy Impact, Notched | 0.600 J/cm² | 2.86 ft-lb/in² | *** 179/2C |
| 0.600 J/cm² @Temperature -30.0 °C | 2.86 ft-lb/in² @Temperature -22.0 °F | *** 179/2C | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 |
| >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | ASTM D257 | |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | ROA; IEC 60093 |
| Dielectric Constant | 3.0 @Frequency 1.00e+6 Hz | 3.0 @Frequency 1.00e+6 Hz | ASTM D150 |
| 3.0 @Frequency 1.00e+6 Hz | 3.0 @Frequency 1.00e+6 Hz | IEC 60250 | |
| Dielectric Strength | 17.0 kV/mm @Thickness 3.20 mm | 432 kV/in @Thickness 0.126 in | in oil; IEC 60243-1 |
| 17.0 kV/mm @Thickness 3.20 mm | 432 kV/in @Thickness 0.126 in | in oil; ASTM D149 | |
| 22.0 kV/mm @Thickness 1.60 mm | 559 kV/in @Thickness 0.0630 in | in oil; IEC 60243-1 | |
| 22.0 kV/mm @Thickness 1.60 mm | 559 kV/in @Thickness 0.0630 in | in oil; ASTM D149 | |
| Dissipation Factor | 0.020 @Frequency 1.00e+6 Hz | 0.020 @Frequency 1.00e+6 Hz | IEC 60250 |
| 0.020 @Frequency 1.00e+6 Hz | 0.020 @Frequency 1.00e+6 Hz | ASTM D150 | |
| Comparative Tracking Index | 575 V | 575 V | IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 27.2 µm/m-°C @Temperature 23.0 - 150 °C | 15.1 µin/in-°F @Temperature 73.4 - 302 °F | *** 11359-2 |
| 40.0 µm/m-°C @Temperature 23.0 - 60.0 °C | 22.2 µin/in-°F @Temperature 73.4 - 140 °F | *** 11359-2 | |
| 82.9 µm/m-°C @Temperature -40.0 - 40.0 °C | 46.1 µin/in-°F @Temperature -40.0 - 104 °F | *** 11359-2 | |
| CTE, linear, Transverse to Flow | 82.2 µm/m-°C @Temperature -40.0 - 40.0 °C | 45.7 µin/in-°F @Temperature -40.0 - 104 °F | *** 11359-2 |
| 100 µm/m-°C @Temperature 23.0 - 60.0 °C | 55.6 µin/in-°F @Temperature 73.4 - 140 °F | *** 11359-2 | |
| 191 µm/m-°C @Temperature 23.0 - 150 °C | 106 µin/in-°F @Temperature 73.4 - 302 °F | *** 11359-2 | |
| Hot Ball Pressure Test | 125 °C | 257 °F | IEC 60695-10-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 200 °C | 392 °F | Flatw 80*10*4 sp=64mm; *** 75/Bf |
| 200 °C @Thickness 3.20 mm | 392 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C | 221 °F | Flatw 80*10*4 sp=64mm; *** 75/Af |
| 105 °C @Thickness 3.20 mm | 221 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| Vicat Softening Point | 135 °C | 275 °F | Rate B/50; ASTM D1525 |
| 135 °C | 275 °F | Rate B/50; *** 306 | |
| 135 °C | 275 °F | Rate B/120; *** 306 | |
| 213 °C | 415 °F | Rate A/50; ASTM D1525 | |
| 213 °C | 415 °F | Rate A/50; *** 306 | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 40.0 - 60.0 °C | 104 - 140 °F | Hopper Temperature |
| Nozzle Temperature | 240 - 260 °C | 464 - 500 °F | Injection Molding |
| Zone 1 | 230 - 245 °C | 446 - 473 °F | |
| Zone 2 | 240 - 255 °C | 464 - 491 °F | |
| Zone 3 | 245 - 265 °C | 473 - 509 °F | |
| Melt Temperature | 250 - 270 °C | 482 - 518 °F | |
| Mold Temperature | 40.0 - 100 °C | 104 - 212 °F | |
| Drying Temperature | 110 - 120 °C | 230 - 248 °F | Injection Molding |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | Injection Molding |
| Moisture Content | 0.020 % | 0.020 % |
本公司长期销售沙伯基础 PBT，PEI，ABS，ASA，EVA，PA6，PBT，PE，PEEK，PET，PMMA，POM，PP，PU，PES，PC料等多种牌号
我司产品均可提供详细物性表(英文和中文版)相关资料；可开13%增值税发票；免费为客户分析样版并提供原料型号咨询服务(可免费帮客户翻译英文资料)；如需试料、了解产品相关信息及当日报价，敬请来电、竭诚为您服务！
为您推荐
在线问
产品参数
- 否
- 美国
- 沙伯基础(原GE)
- VX4915R
- 品牌经销
- 标准料
- 注塑级
- 标准级
- 汽车部件、 电子电器部件、 运动器材、 家电部件、 电动工具配件