帝人PC经销商 1250Y/1225Y/1225L/1250Z/1225Z/
- ¥21.00 ≥25千克起批
参数
- 嘉兴帝人厂家(产地)
- L-1225L牌号
- 注塑级加工级别
广东 东莞
不限
产品详情
产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 吸水率 | 24hr，in 23℃ | ASTM D-570 | 0.20 | % |
| 阻燃性 | 厚度1.47mm (厚度3.05mm ) | UL 94 | 94V-2 | |
| 透光率 | 厚度3mm | ASTM D-1003 | 88 | % |
| 比重 | ASTM D-792 | 1.20 | ||
| 弯曲模量 | ASTM D-790 | 2280(23300) | Mpa(kgf/cm2) | |
| 耐冲击强度值 | 艾氏、带缺口厚度3.2mm | ASTM D-256 | 780(80) | j/m(kgf.cm/cm) |
| 拉伸强度(屈服点) | - | ASTM D-638 | 63(640) | Mpa(kgf/cm2) |
| 拉伸强度(断裂点) | - | ASTM D-638 | 74(750) | Mpa(kgf/cm2) |
| 弯曲强度 | ASTM D-790 | 90(920) | Mpa(kgf/cm2) | |
| 拉伸模量 | ASTM D-638 | 2170(22100) | Mpa(kgf/cm2) | |
| 耐冲击强度值 | 艾氏、带缺口厚度6.4mm | ASTM D-256 | 100(10) | j/m(kgf.cm/cm) |
| 洛氏硬度 | ASTM D-785 | 77 | M标度 | |
| 压缩强度 | ASTM D-695 | 77(790) | Mpa(kgf/cm2) | |
| 拉伸率(屈服点) | - | ASTM D-638 | 6 | - |
| 拉伸率(断裂点) | - | ASTM D-638 | 140 | - |
| 折射率 | ASTM D-542 | 1.585 | ||
| 耐导电径迹性 | CTI | IEC 112 | 300 | V |
| 体积电阻率 | ASTM D-257 | 3 | 1016Ω.cm | |
| 绝缘破坏强度 | 快速加压值厚度1.6mm | ASTM D-149 | 30 | KV/mm |
| 介电率 | 60Hz(106Hz) | ASTM D-150 | 2.95(2.9) | |
| 介电正切 | 60Hz(106Hz) | ASTM D-150 | 0.0004(0.009) | |
| 耐电弧性 | ASTM D-495 | 110 | sec | |
| 成型收缩率 | 流动方向(垂直方向) | ASTM D-955 | 0.5～0.7 | % |
| 负荷挠曲温度 | 负荷0.451MPa(4.6kgf/cm) | ASTM D-648 | 141 | ℃ |
| 温度指数(电学式) | 厚度1.47mm | UL 746B | 125 | °C |
| 温度指数(冲击式) | 厚度1.47mm | UL 746B | 115 | °C |
| 温度指数(非冲击式) | 厚度1.47mm | UL 746B | 125 | °C |
| 负荷挠曲温度 | 负荷1.813MPa(18.6kgf/cm) | ASTM D-648 | 131 | ℃ |
| 线膨胀系数 | 流动方向(垂直方向) | ASTM D-696 | 7 | 10-5cm/cm/℃ |
| PC L-1225L 帝人化成公司物性数据 |
| 规格级别： | --- | 外观颜色： | --- |
| 用途概述： | 用途：超薄壁型电器、电子元件。 | ||
| 备注说明： | --- | ||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||||||||||||||||
| 基本性能 | 吸水率 | 24hr，in 23℃ | ASTM D-570 | 0.20 | % | |||||||||||||||
| 物理性能 | 比重 | --- | ASTM D-792 | 1.20 | --- | |||||||||||||||
| 透光率 | 厚度3mm | ASTM D-1003 | 88 | % | ||||||||||||||||
| 阻燃性 | 厚度1.47mm | UL 94 | 94V-2 | --- | ||||||||||||||||
| 阻燃性 | 厚度3.05mm | UL 94 | 94V-2 | --- | ||||||||||||||||
| 机械性能 | 折射率 | --- | ASTM D-542 | 1.585 | --- | |||||||||||||||
| --- |
|
|
| ||||||||||||||||
| 拉伸模量 | --- | ASTM D-638 | 2170(22100) | Mpa(kgf/cm2) | ||||||||||||||||
| --- |
|
| --- | ||||||||||||||||
| 弯曲强度 | --- | ASTM D-790 | 90(920) | Mpa(kgf/cm2) | ||||||||||||||||
| 弯曲模量 | --- | ASTM D-790 | 2280(23300) | Mpa(kgf/cm2) | ||||||||||||||||
| 压缩强度 | --- | ASTM D-695 | 77(790) | Mpa(kgf/cm2) | ||||||||||||||||
| 耐冲击强度值 | 艾氏、带缺口厚度3.2mm | ASTM D-256 | 780(80) | j/m(kgf.cm/cm) | ||||||||||||||||
| 耐冲击强度值 | 艾氏、带缺口厚度6.4mm | ASTM D-256 | 100(10) | j/m(kgf.cm/cm) | ||||||||||||||||
| 洛氏硬度 | --- | ASTM D-785 | 77 | M标度 | ||||||||||||||||
| 电气性能 | 耐导电径迹性（CTI） | --- | IEC 112 | 300 | V | |||||||||||||||
| 绝缘破坏强度 | 快速加压值厚度1.6mm | ASTM D-149 | 30 | KV/mm | ||||||||||||||||
| 体积电阻率 | --- | ASTM D-257 | 3 | 1016Ω.cm | ||||||||||||||||
| 介电率 | 60Hz | ASTM D-150 | 2.95 | --- | ||||||||||||||||
| 介电率 | 106Hz | ASTM D-150 | 2.9 | --- | ||||||||||||||||
| 介电正切 | 60Hz | ASTM D-150 | 0.0004 | --- | ||||||||||||||||
| 介电正切 | 106Hz | ASTM D-150 | 0.009 | --- | ||||||||||||||||
| 耐电弧性 | --- | ASTM D-495 | 110 | sec | ||||||||||||||||
| 加工性能 |
| --- |
|
|
| |||||||||||||||
| 热 性 能 | 负荷挠曲温度 | 负荷0.451MPa(4.6kgf/cm) | ASTM D-648 | 141 | °C | |||||||||||||||
| 负荷挠曲温度 | 负荷1.813MPa(18.6kgf/cm) | ASTM D-648 | 131 | °C | ||||||||||||||||
| --- |
|
|
| ||||||||||||||||
|
|
|
|
| ||||||||||||||||