| 物理性能 | 比重 | ASTMD792 | 1.20 | g/cm | |
| 密度 | ***1183 | 1.20 | g/cm | ||
| 熔流率（熔体流动速率）(300°C/1.2kg) | ASTMD1238 | 7.0 | g/10min | ||
| 溶化体积流率（MVR）(300°C/1.2kg) | ***1133 | 7.00 | cm/10min | ||
| 收缩率-流动(3.20mm) | InternalMethod | 0.60to0.80 | % | ||
| 吸水率(饱和,23°C) | ***62 | 0.35 | % | ||
| 吸水率(平衡,23°C,50%RH) | ***62 | 0.15 | % |
| 冲击性能 | 悬壁梁缺口冲击强度(23°C) | ASTMD256 | 150 | J/m | |
| NotchedIzodImpactStrength8(23°C) | ***180/1A | 15 | kJ/m | ||
| 装有测量仪表的落镖冲击(23°C,TotalEnergy) | ASTMD3763 | 70.0 | J | ||
| 热性能 | HeatDeflectionTemperature9(0.45MPa,Unannealed,64.0mmSpan) | ***75-2/Bf | 135 | °C | |
| 载荷下热变形温度(1.8MPa,未退火,3.20mm) | ASTMD648 | 125 | °C | ||
| HeatDeflectionTemperature9(1.8MPa,Unannealed,64.0mmSpan) | ***75-2/Af | 123 | °C | ||
| 维卡软化温度 | ASTMD152510 | 141 | °C | ||
| BallPressureTest(125°C) | IEC60695-10-2 | Pass | |||
| 线形热膨胀系数-流动(-40到40°C) | ASTME831 | 6.8E-5 | cm/cm/°C | ||
| 线形热膨胀系数-横向(-40到40°C) | ASTME831 | 6.7E-5 | cm/cm/°C | ||
| RTIElec | UL746 | 125 | °C | ||
| RTIImp | UL746 | 115 | °C | ||
| RTIStr | UL746 | 125 | °C | ||
| 电气性能 | 相比耐漏电起痕指数(CTI) | UL746 | PLC3 | ||
| 高电弧燃烧指数(HAI) | UL746 | PLC1 | |||
| 热丝引燃(HWI) | UL746 | PLC3 | |||
| 可燃性 | UL阻燃等级(1.5mm) | UL94 | V-0 | ||
| 灼热丝易燃指数(1.0mm) | IEC60695-2-12 | 960 | °C | ||
| 热灯丝点火温度 | 1.0mm | IEC60695-2-13 | 850 | °C | |
| 1.5mm | IEC60695-2-13 | 850 | °C |
PC塑胶原料它是一种***的热塑性塑料，透明的度达90%，被誉为是透明金属。它刚硬而具有韧性，具有较高的冲击强度，高度的尺寸稳定性和范围很宽的使用温度、良好的电绝缘性能及耐热性和***性，可以通过注射、挤出成型。PC塑料的热性能***，可在-100℃-130℃之间长期使用，脆化温度在-100℃以下。
虽然聚碳酸酯具有耐开裂和耐药品性较差，高温易水解，与其它树脂的相容性差，润滑性能不好，但是，可以通过加入其它的树脂或者无机填充剂进行改性，从而获得十分***的性能。