韩国乐天无卤阻燃高耐热PC INFINO GC-1022U
Density / Specific Gravity(Natural) | 1.18 | g/cm | ASTM D792,ISO 1183 |
Melt Mass-Flow Rate (MFR)(250°C/10.0 kg) | 19 | g/10 min | ASTM D1238,ISO 1133 |
Molding Shrinkage | |||
Flow : 3.20 mm | 0.40 to 0.70 | % | ASTM D955 |
Across Flow : 3.20 mm | 0.40 to 0.70 | % | ASTM D955 |
Across Flow : 2.00 mm | 0.40 to 0.70 | % | ISO 294-4 |
Flow : 2.00 mm | 0.40 to 0.70 | % | ISO 294-4 |
Hardness | Nominal Value | Unit | Test Method |
Rockwell Hardness(R-Scale) | 118 | ASTM D785,ISO 2039-2 |
Charpy Notched Impact Strength5(23°C) | 64 | kJ/m | ISO 179/1eA |
Notched Izod Impact | |||
23°C, 3.18 mm | 690 | J/m | ASTM D256 |
23°C5 | 58 | kJ/m | ISO 180/1A |
Thermal | Nominal Value | Unit | Test Method |
Deflection Temperature Under Load | |||
1.8 MPa, Unannealed, 6.40 mm | 127 | °C | ASTM D648 |
1.8 MPa, Unannealed, 4.00 mm | 120 | °C | ISO 75-2/A |
Vicat Softening Temperature | 143 | °C | ISO 306/B50 |
Flammability | Nominal Value | Test Method | |
Flame Rating | UL 94 | ||
0.75 mm | V-2 | ||
1.5 mm | V-0 | ||
3.0 mm | V-0 |
PC耐热,抗冲击,阻燃,在普通使用温度内都有良好的机械性能。同性能接近聚甲基丙烯酸甲酯相比,聚碳酸酯的耐冲击性能好,折射***,加工性 能好,不需要添加剂就具有UL94 V-0级阻燃性能。但是聚甲基丙烯酸甲酯相对聚碳酸酯较低,并可通过本体聚合的方法生产大型的器件。随着聚碳酸酯生产规模的日益扩大,聚碳酸酯同聚甲 基丙烯酸甲酯之间的差异在日益缩小。聚碳酸酯的***性差。一些用于易磨损用途的聚碳酸酯器件需要对表面进行特殊处理。