耐低温水解PC LEXAN EXL1414H
¥46.50
9%GF增强PC LEXAN EXL4419耐-40度
¥46.50
耐低温-40度PC LEXAN EXL1414
¥46.50
PC LEXAN EXL1112T透明耐低温冲击
¥36.50
耐低温食品级PC LEXAN EXL1890T
¥36.50
代理沙伯基础***高流动耐低温PC LEXAN EXL1132
| 比重 | |||
| -- | 1.18 | g/cm | ASTM D792 |
| -- | 1.19 | g/cm | *** 1183 |
| 熔流率（熔体流动速率）(300°C/1.2 kg) | 17 | g/10 min | ASTM D1238 |
| 溶化体积流率（MVR）(300°C/1.2 kg) | 16.0 | cm/10min | *** 1133 |
| 拉伸模量 | |||
| --1 | 2280 | MPa | ASTM D638 |
| -- | 2150 | MPa | *** 527-2/1 |
| 抗张强度 | |||
| 屈服2 | 58.1 | MPa | ASTM D638 |
| 屈服 | 57.0 | MPa | *** 527-2/50 |
| 断裂3 | 58.7 | MPa | ASTM D638 |
| 断裂 | 55.0 | MPa | *** 527-2/50 |
| 简支梁缺口冲击强度9 | *** 179/1eA | ||
| -30°C | 25 | kJ/m | *** 179/1eA |
| 23°C | 60 | kJ/m | *** 179/1eA |
| 简支梁无缺口冲击强度10 | *** 179/1eU | ||
| -30°C | 无断裂 | *** 179/1eU | |
| 23°C | 无断裂 | *** 179/1eU | |
| 悬壁梁缺口冲击强度 | |||
| -30°C | 670 | J/m | ASTM D256 |
| 23°C | 750 | J/m | ASTM D256 |
| -30°C11 | 20 | kJ/m | *** 180/1A |
| 23°C12 | 55 | kJ/m | *** 180/1A |
| 载荷下热变形温度 | |||
| 0.45 MPa, 未退火, 3.20 mm | 137 | °C | ASTM D648 |
| 0.45 MPa, 退火14 | 136 | °C | *** 75-2/Be |
| 1.8 MPa, 未退火, 3.20 mm | 124 | °C | ASTM D648 |
| 1.8 MPa, 未退火, 100 mm 跨距15 | 125 | °C | *** 75-2/Ae |