代理科思创抗紫外线PC MAKROLON AG2677
Density(23°C) | 1.20 | g/cm | *** 1183 |
Apparent (Bulk) Density3 | 0.66 | g/cm | *** 60 |
Melt Mass-Flow Rate (MFR)(300°C/1.2 kg) | 13 | g/10 min | *** 1133 |
Melt Volume-Flow Rate (MVR)(300°C/1.2 kg) | 12 | cm/10min | *** 1133 |
Molding Shrinkage | |||
Across Flow | 0.60 to 0.80 | % | *** 2577 |
Flow | 0.60 to 0.80 | % | *** 2577 |
Across Flow : 280°C, 2.00 mm4 | 0.75 | % | *** 294-4 |
Flow : 2.00 mm4 | 0.70 | % | *** 294-4 |
Water Absorption | *** 62 | ||
Saturation, 23°C | 0.30 | % | |
Equilibrium, 23°C, 50% RH | 0.12 | % | |
| Hardness | Nominal Value | Unit | Test Method |
Ball Indentation Hardness | 116 | MPa | *** 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus(23°C) | 2400 | MPa | *** 527-2/1 |
Tensile Stress | *** 527-2/50 | ||
Yield, 23°C | 67.0 | MPa | |
Break, 23°C | 70.0 | MPa |
Charpy Notched Impact Strength7 | *** 179/1eA | ||
-30°C, Complete Break | 14 | kJ/m | |
23°C, Partial Break | 70 | kJ/m |
Notched Izod Impact Strength7 | *** 180/A | ||
-30°C, Complete Break | 15 | kJ/m | |
23°C, Partial Break | 70 | kJ/m |
Heat Deflection Temperature | |||
0.45 MPa, Unannealed | 136 | °C | *** 75-2/B |
1.8 MPa, Unannealed | 124 | °C | *** 75-2/A |
Glass Transition Temperature8 | 144 | °C | *** 11357-2 |