***科思创***202度PC APEC 2097抗UV
Density(23°C) | 1.13 | g/cm | ISO 1183 |
Melt Mass-Flow Rate (MFR)(330°C/2.16 kg) | 8.0 | g/10 min | ISO 1133 |
Melt Volume-Flow Rate (MVR)(330°C/2.16 kg) | 8.0 | cm/10min | ISO 1133 |
Molding Shrinkage3 | ISO 294-4 | ||
Across Flow : 2.00 mm | 0.90 | % | |
Flow : 2.00 mm | 0.90 | % |
Tensile Modulus(23°C) | 2450 | MPa | ISO 527-2/1 |
Tensile Stress(Yield, 23°C) | 76.0 | MPa | ISO 527-2/50 |
Tensile Strain(Yield, 23°C) | 6.9 | % | ISO 527-2/50 |
Nominal Tensile Strain at Break(23°C) | > 50 | % | ISO 527-2/50 |
Flexural Modulus4(23°C) | 2450 | MPa | ISO 178 |
Flexural Stress4(23°C) | 110 | MPa | ISO 178 |
Heat Deflection Temperature | |||
0.45 MPa, Unannealed | 191 | °C | ISO 75-2/B |
1.8 MPa, Unannealed | 172 | °C | ISO 75-2/A |
Vicat Softening Temperature | 202 | °C | ISO 306/B120 |
CLTE | ISO 11359-2 | ||
Flow : 23 to 55°C | 6.5E-5 | cm/cm/°C | |
Transverse : 23 to 55°C | 6.5E-5 | cm/cm/°C | |
RTI Elec | 150 | °C | UL 746 |
RTI Imp | 130 | °C | UL 746 |
RTI Str | 150 | °C | UL 746 |
Flame Rating(1.5 mm) | HB | UL 94 | |
Glow Wire Flammability Index | 800 | °C | IEC 60695-2-12 |
Oxygen Index5 | 25 | % | ISO 4589-2 |