PC沙特基础塑料500ECR
------
防火PC沙伯基础塑料500ECR-131玻纤增强10%
------
SABIC Lexan 500ECR
Polymer,Thermoplastic,Polycarbonate (PC)
SABIC Innovative Plastics (GE Plastics)
Lexan 500ECR Polycarbonate (PC) resin is a 10% glass fiber filled, injection moldable grade. It is of non-chlorinated & non-brominated flame retardant systems with UL-94 V0 rating at 2.3mm. It is available in various opaque color options designed for applications requiring improved stiffness.
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 比重 | 1.27 g/cc | 1.27 g/cc | ASTM D792 |
| 密度 | 1.25 g/cc | 0.0452 lb/in³ | ISO 1183 |
| 水分吸收 | 0.130 % | 0.130 % | 23°C / 50% RH; ISO 62 |
| 饱和吸水率 | 0.31 % | 0.31 % | ISO 62 |
| 线性成型收缩率,Flow | 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm | 0.0040 - 0.0060 in/in @Thickness 0.126 in | SABIC Method |
| 线性成型收缩率，横向 | 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm | 0.0040 - 0.0060 in/in @Thickness 0.126 in | SABIC Method |
| 熔体流动速率 | 7.5 g/10 min @Load 1.20 kg, Temperature 300 °C | 7.5 g/10 min @Load 2.65 lb, Temperature 572 °F | ASTM D1238 |
| 化合物熔体指数 | 7.0 g/10 min @Load 1.20 kg, Temperature 300 °C | 7.0 g/10 min @Load 2.65 lb, Temperature 572 °F | MVR [cm^3/10 min]; ISO 1133 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 硬度，H358/30 | 115 MPa | 16700 psi | ISO 2039-1 |
| 抗张强度(断裂) | 45.0 MPa | 6530 psi | 5 mm/min; ISO 527 |
---------