20%GF/5%PTFE耐磨PC LUBRICOMP DFL14美国SABIC
Density / Specific Gravity |
| g/cm³ | ASTM D792 |
Molding Shrinkage | ASTM D955 | ||
Flow : 24 hr | 0.20 to 0.40 | % | |
Across Flow : 24 hr | 0.50 to 0.70 | % | |
Water Absorption | |||
24 hr, 23°C, 50% RH | 0.12 | % | ASTM D570 |
Equilibrium, 23°C, 50% RH | 0.19 | % | *** 62 |
Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus | |||
-- 2 | 6320 | MPa | ASTM D638 |
-- | 6020 | MPa | *** 527-1/1 |
Tensile Strength | |||
Yield 3 | 96.0 | MPa | ASTM D638 |
Yield | 96.0 | MPa | *** 527-2/5 |
Break 3 | 94.0 | MPa | ASTM D638 |
Break | 94.0 | MPa | *** 527-2/5 |
Tensile Elongation |
Notched Izod Impact | |||
23°C | 150 | J/m | ASTM D256 |
23°C 7 | 15 | kJ/m² | *** 180/1A |