SABIC LEXAN EXL1434T耐低温抗紫外线耐冲击PC
Density / Specific Gravity | 1.19 | g/cm³ | ASTM D792, ISO 1183 |
Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 10 | g/10 min | ASTM D1238 |
Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 9.0 | cm³/10min | ISO 1133 |
Molding Shrinkage | Internal Method | ||
Across Flow : 3.20 mm | 0.40 to 0.80 | % | |
Flow : 3.20 mm | 0.40 to 0.80 | % | |
Water Absorption | ISO 62 | ||
Saturation, 23°C | 0.12 | % | |
Equilibrium, 23°C, 50% RH | 0.090 | % | |
Hardness | Nominal Value | Unit | Test Method |
Rockwell Hardness (L-Scale) | 87 | ISO 2039-2 |
Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus | |||
-- 3 | 2180 | MPa | ASTM D638 |
-- | 2300 | MPa | ISO 527-1/1 |
Tensile Strength | |||
Yield 4 | 57.0 | MPa | ASTM D638 |
Yield | 56.0 | MPa | ISO 527-2/50 |
Break 4 | 59.0 | MPa | ASTM D638 |
Break | 55.0 | MPa | ISO 527-2/50 |
Tensile Elongation | |||
Yield 4 | 5.6 | % | ASTM D638 |
Yield | 5.4 | % | ISO 527-2/50 |
Break 4 | 120 | % | ASTM D638 |
Break | 110 | % | ISO 527-2/50 |
Flexural Modulus | |||
50.0 mm Span 5 | 2180 | MPa | ASTM D790 |
-- 6 | 2120 | MPa | ISO 178 |
Flexural Stress | |||
-- 6, 7 | 88.0 | MPa | ISO 178 |
Yield, 50.0 mm Span 5 | 92.0 | MPa | ASTM D790 |
Impact | Nominal Value | Unit | Test Method |
Charpy Notched Impact Strength 8 | ISO 179/1eA | ||
-30°C | 60 | kJ/m² | |
23°C | 70 | kJ/m² |