产品说明:
Unfilled PBT+PC alloy. Outstanding low temperature impact/chemical resistance. UV stabilized version of XENOY
物性信息:
基本信息 | |
---|---|
黄卡编号 |
|
添加剂 |
|
特性 |
|
加工方法 |
|
物理性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
比重 | 1.17 | g/cm³ | ASTM D792, ISO 1183 |
特定体积 | 0.850 | cm³/g | ASTM D792 |
熔流率(熔体流动速率) | |||
250°C/2.16 kg | 3.8 | g/10 min | ASTM D1238, ISO 1133 |
250°C/5.0 kg | 11 | g/10 min | ASTM D1238, ISO 1133 |
265°C/2.16 kg | 6.8 | g/10 min | ASTM D1238 |
266°C/5.0 kg | 20 | g/10 min | ASTM D1238 |
溶化体积流率(MVR) | ISO 1133 | ||
250°C/2.16 kg | 3.60 | cm³/10min | ISO 1133 |
250°C/5.0 kg | 10.9 | cm³/10min | ISO 1133 |
265°C/2.16 kg | 6.50 | cm³/10min | ISO 1133 |
265°C/5.0 kg | 18.9 | cm³/10min | ISO 1133 |
收缩率 - 流动 (3.20 mm) | 1.0 到 1.2 | % | 内部方法 |
吸水率 | ISO 62 | ||
饱和, 23°C | 0.28 | % | ISO 62 |
平衡, 23°C, 50% RH | 0.080 | % | ISO 62 |
机械性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
拉伸模量 | |||
-- 1 | 1830 | MPa | ASTM D638 |
-- 2 | 1830 | MPa | 内部方法 |
-- 3 | 1820 | MPa | ASTM D638 |
-- | 1800 | MPa | ISO 527-2/1 |
抗张强度 | |||
屈服 4 | 44.0 | MPa | ASTM D638 |
屈服 5 | 45.0 | MPa | 内部方法 |
屈服 6 | 47.0 | MPa | ASTM D638 |
屈服 | 44.0 | MPa | ISO 527-2/5 |
屈服 | 47.0 | MPa | ISO 527-2/50 |
断裂 7 | 50.0 | MPa | ASTM D638 |
断裂 8 | 47.0 | MPa | 内部方法 |
断裂 9 | 48.0 | MPa | ASTM D638 |
断裂 | 43.0 | MPa | ISO 527-2/5, ISO 527-2/50 |
伸长率 | |||
屈服 10 | 4.6 | % | ASTM D638 |
屈服 11 | 4.6 | % | 内部方法 |
屈服 12 | 4.0 | % | ASTM D638 |
屈服 | 4.1 | % | ISO 527-2/5 |
屈服 | 4.6 | % | ISO 527-2/50 |
断裂 13 | 120 | % | ASTM D638 |
断裂 14 | 110 | % | 内部方法 |
断裂 15 | 120 | % | ASTM D638 |
断裂 | 110 | % | ISO 527-2/5 |
断裂 | 120 | % | ISO 527-2/50 |
弯曲模量 | |||
50.0 mm 跨距 16 | 1660 | MPa | ASTM D790 |
-- 17 | 1870 | MPa | ISO 178 |
弯曲应力 | |||
-- | 71.0 | MPa | ISO 178 |
屈服, 50.0 mm 跨距 18 | 70.0 | MPa | ASTM D790 |
断裂, 50.0 mm 跨距 19 | 69.0 | MPa | ASTM D790 |
冲击性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
简支梁缺口冲击强度 20 | ISO 179/1eA | ||
-30°C | 48 | kJ/m² | ISO 179/1eA |
23°C | 56 | kJ/m² | ISO 179/1eA |
悬壁梁缺口冲击强度 | |||
-40°C | 600 | J/m | ASTM D256 |
-30°C | 650 | J/m | ASTM D256 |
-20°C | 700 | J/m | ASTM D256 |
-10°C | 660 | J/m | ASTM D256 |
0°C | 690 | J/m | ASTM D256 |
23°C | 720 | J/m | ASTM D256 |
-40°C 21 | 46 | kJ/m² | ISO 180/1A |
-30°C 22 | 48 | kJ/m² | ISO 180/1A |
-20°C 23 | 50 | kJ/m² | ISO 180/1A |
-10°C 24 | 52 | kJ/m² | ISO 180/1A |
0°C 25 | 55 | kJ/m² | ISO 180/1A |
23°C 26 | 56 | kJ/m² | ISO 180/1A |
装有测量仪表的落镖冲击 | ASTM D3763 | ||
-40°C, Energy at Peak Load | 49.5 | J | ASTM D3763 |
-40°C, Total Energy | 59.2 | J | ASTM D3763 |
-30°C, Energy at Peak Load | 49.5 | J | ASTM D3763 |
-30°C, Total Energy | 61.9 | J | ASTM D3763 |
-20°C, Energy at Peak Load | 41.9 | J | ASTM D3763 |
-20°C, Total Energy | 53.2 | J | ASTM D3763 |
23°C, Energy at Peak Load | 44.8 | J | ASTM D3763 |
23°C, Total Energy | 54.0 | J | ASTM D3763 |
热性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
载荷下热变形温度 | |||
0.45 MPa, 未退火, 3.20 mm | 108 | °C | ASTM D648 |
0.45 MPa, 未退火, 6.40 mm | 117 | °C | ASTM D648 |
0.45 MPa, 未退火, 64.0 mm 跨距 27 | 110 | °C | ISO 75-2/Bf |
1.8 MPa, 未退火, 3.20 mm | 83.5 | °C | ASTM D648 |
1.8 MPa, 未退火, 6.40 mm | 95.9 | °C | ASTM D648 |
1.8 MPa, 未退火, 64.0 mm 跨距 28 | 87.0 | °C | ISO 75-2/Af |
维卡软化温度 | |||
-- | 120 | °C | ASTM D1525, ISO 306/B50 15 29 |
-- | 122 | °C | ISO 306/B120 |
线形热膨胀系数 | |||
流动 : -40 到 95°C | 9.8E-5 | cm/cm/°C | ASTM E831 |
流动 : -30 到 80°C | 9.8E-5 | cm/cm/°C | ISO 11359-2 |
横向 : -40 到 95°C | 1.0E-4 | cm/cm/°C | ASTM E831 |
横向 : -30 到 80°C | 1.0E-4 | cm/cm/°C | ISO 11359-2 |
注射 | 额定值 | 单位制 | |
---|---|---|---|
干燥温度 | 110 | °C | |
干燥时间 | 4.0 到 6.0 | hr | |
干燥时间, | 8.0 | hr | |
建议的水分含量 | 0.020 | % | |
建议注射量 | 50 到 80 | % | |
料筒后部温度 | 243 到 266 | °C | |
料筒中部温度 | 249 到 271 | °C | |
料筒前部温度 | 254 到 277 | °C | |
射嘴温度 | 254 到 271 | °C | |
加工(熔体)温度 | 260 到 277 | °C | |
模具温度 | 65.6 到 87.8 | °C | |
背压 | 0.345 到 0.689 | MPa | |
螺杆转速 | 50 到 80 | rpm | |
排气孔深度 | 0.013 到 0.020 | mm |