PC / ABS has excellent comprehensive performance, but its chemical resistance is poor and it is easy to be eroded by strong chemical solvents, resulting in product cracking and other defects. Especially when PC / ABS products are sprayed with some body exterior paint, due to the strong corrosivity of its solvent, the products are prone to stress marks, cracking and even cracking. In view of this situation, Youchang Jinhu has developed a new generation of chemical solvent resistant PC / ABS. After simulating the stress corrosion of chemical solvent, the crack generation time of this material is three times higher than that of ordinary PC / ABS.
PC/ABS的综合性能优良,但是其耐化学品性能差而容易受到比较强的化学溶剂侵蚀而导致制品开裂等缺陷。特别是当PC/ABS 制品喷涂某些车身外饰漆时,由于其溶剂的强腐蚀性,易导致制品出现应力痕,龟裂,甚至开裂。优畅锦湖针对这种情况,开发了***耐化学溶剂的PC/ABS,这种材料经过了模拟化学品溶剂的应力侵蚀,其产生裂纹的时间比普通PC/ABS 提高了3倍。