8%碳纤导电PC/ABS STAT-KON JK800美国SABIC
- ¥48.00 25 - 999千克
- ¥47.00 ≥1000千克
参数
- 导电PC合金产品特性
- 否是否进口
- 美国产地
广东 深圳
1天内发货
3000千克
美国SABIC导电PC STAT-KON DD000
¥45.00
产品详情
8%碳纤导电PC/ABS STAT-KON JK800美国SABIC
Density / Specific Gravity | 1.25 | g/cm³ | ASTM D792 |
Melt Mass-Flow Rate (MFR) (260°C/2.16 kg) | 17 | g/10 min | ASTM D1238 |
Molding Shrinkage | Internal Method | ||
Across Flow : 3.20 mm | 0.20 to 0.40 | % | |
Flow : 3.20 mm | 0.10 to 0.20 | % |
| Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus | |||
-- 1 | 7580 | MPa | ASTM D638 |
-- | 7500 | MPa | *** 527-1/1 |
Tensile Strength | |||
Yield 2 | 96.0 | MPa | ASTM D638 |
Yield | 95.0 | MPa | *** 527-2/5 |
Break 2 | 96.0 | MPa | ASTM D638 |
Break | 95.0 | MPa | *** 527-2/5 |
Notched Izod Impact | |||
23°C | 37 | J/m | ASTM D256 |
23°C 6 | 4.0 | kJ/m² | *** 180/1A |
Unnotched Izod Impact | |||
23°C | 350 | J/m | ASTM D4812 |
23°C 6 | 21 | kJ/m² | *** 180/1U |
Instrumented Dart Impact (23°C, Total Energy) | 82.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
Deflection Temperature Under Load | ASTM D648 | ||
0.45 MPa, Unannealed, 3.20 mm | 97.0 | °C | |
1.8 MPa, Unannealed, 3.20 mm | 92.0 | °C | |
1.8 MPa, Unannealed, 6.40 mm | 94.0 | °C |