Density / Specific Gravity | 1.11 | g/cm³ | ASTM D792, *** 1183 |
Melt Mass-Flow Rate (MFR) | ASTM D1238, *** 1133 | ||
230°C/3.8 kg | 4.5 | g/10 min | |
260°C/5.0 kg | 25 | g/10 min | |
Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
Rockwell Hardness (R-Scale) | 112 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus 4 | 2210 | MPa | ASTM D638 |
Tensile Strength 5 (Yield) | 50.3 | MPa | ASTM D638 |
Tensile Elongation 5 | ASTM D638 | ||
Yield | 4.0 | % | |
Break | 50 | % | |
Flexural Modulus | 2340 | MPa | ASTM D790 |
Flexural Strength | 80.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
Notched Izod Impact | ASTM D256 | ||
-30°C | 290 | J/m | |
23°C | 480 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
Deflection Temperature Under Load | ASTM D648 | ||
0.45 MPa, Unannealed | 116 | °C | |
1.8 MPa, Unannealed | 95.0 | °C | |
Vicat Softening Temperature | 133 | °C | ASTM D1525 6 |
CLTE - Flow (-40 to 40°C) | 7.6E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
Flame Rating 7 (1.0 mm) | HB | UL 94 |