产品说明 | |
Copolyester DN004 has been tested for FDA/ISO 10993 and USP Class VI Biological Evaluation testing after Gamma and EtO sterilization. Eastar copolyesters are brilliantly clear polymers that have excellent impact strength, chemical resistance, dimensional stability, and low shrinkage rates. Eastar DN004 copolyesters are the toughest materials for the cosmetics and personal care packaging applications. It's very shatter resistant and offers excellent chemical resistance. DN004 contains a mold release. |
总体 | |
材料状态 |
|
资料1 | Processing - Injection Molding Guide (English)Technical Datasheet (English) |
搜索 UL 黄卡 |
|
供货地区 | 北美洲非洲和中东拉丁美洲欧洲亚太地区 |
特性 | 共聚物抗撞击性,高可加工性,良好快的成型周期耐化学性良好耐热性,高***性清晰度,高韧性良好食品接触的合规性水解稳定外观良好无定形的 |
用途 | 大型家用电器和小型家用电器电器用具家用货品消费品应用领域 |
机构评级 | FDA 食品接触, 未评级NSF 51 |
加工方法 |
|
物理性能 | 额定值 | 单位制 | 测试方法 |
密度 / 比重 | 1.17 | g/cm | ASTM D792 |
收缩率 - 流动 | 0.50 到 0.70 | % | ASTM D955 |
硬度 | 额定值 | 单位制 | 测试方法 |
洛氏硬度(R 级, 23°C) | 115 | ASTM D785 |
机械性能 | 额定值 | 单位制 | 测试方法 |
拉伸模量(23°C) | 1620 | MPa | ASTM D638,ISO 527-2 |
抗张强度 | |||
屈服, 23°C | 44.0 | MPa | ASTM D638 |
屈服, 23°C | 45.0 | MPa | ISO 527-2 |
断裂, 23°C | 53.0 | MPa | ASTM D638 |
断裂, 23°C | 49.0 | MPa | ISO 527-2 |
伸长率 | |||
屈服, 23°C | 7.0 | % | ASTM D638,ISO 527-2 |
断裂, 23°C | 140 | % | ASTM D638 |
断裂, 23°C | 130 | % | ISO 527-2 |
弯曲模量 | |||
23°C | 1590 | MPa | ASTM D790 |
23°C | 1530 | MPa | ISO 178 |
弯曲强度(屈服, 23°C) | 66.0 | MPa | ASTM D790 |
冲击性能 | 额定值 | 单位制 | 测试方法 |
悬壁梁缺口冲击强度 | |||
23°C | 650 | J/m | ASTM D256 |
-40°C | 14 | kJ/m | ISO 180 |
23°C | 66 | kJ/m | ISO 180 |
无缺口悬臂梁冲击(23°C) | 无断裂 | ASTM D4812 |
热性能 | 额定值 | 单位制 | 测试方法 |
载荷下热变形温度 | ASTM D648 | ||
0.45 MPa, 未退火 | 109 | °C | |
1.8 MPa, 未退火 | 92.0 | °C |
光学性能 | 额定值 | 单位制 | 测试方法 |
透射率(总计) | 92.0 | % | ASTM D1003 |
雾度 | <1.0 | % | ASTM D1003 |
注射 | 额定值 | 单位制 | |
干燥温度 | 88 | °C | |
干燥时间 | 4.0 到 6.0 | hr | |
加工(熔体)温度 | 260 到 282 | °C | |
模具温度 | 38 到 66 | °C |
备注 |
.