美国Sabic 30GF增强PEI ULTEM 2310
30% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing.
Density / Specific Gravity | 1.51 | g/cm | ASTM D792 |
Melt Mass-Flow Rate (MFR)(337°C/6.6 kg) | 7.6 | g/10 min | ASTM D1238 |
Molding Shrinkage | Internal Method | ||
Across Flow : 3.20 mm | 0.20 to 0.40 | % | |
Flow : 3.20 mm | 0.20 to 0.40 | % |
| Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus2 | 9230 | MPa | ASTM D638 |
Tensile Strength3 | ASTM D638 | ||
Yield | 168 | MPa | |
Break | 158 | MPa | |
Tensile Elongation3(Break) | 2.0 | % | ASTM D638 |
Flexural Modulus4(100 mm Span) | 9230 | MPa | ASTM D790 |
Flexural Strength4(Break, 100 mm Span) | 220 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
Notched Izod Impact(23°C) | 85 | J/m | ASTM D256 |
Reverse Notch Izod Impact(3.20 mm) | 440 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
Deflection Temperature Under Load(1.8 MPa, Unannealed, 6.40 mm) | 210 | °C | ASTM D648 |
CLTE | ASTM E831 | ||
Flow : -20 to 150°C | 1.6E-5 | cm/cm/°C | |
Transverse : -20 to 150°C | 4.1E-5 | cm/cm/°C | |
RTI Elec | 180 | °C | UL 746 |
RTI Imp | 170 | °C | UL 746 |
RTI Str | 180 | °C | UL 746 |
| Electrical | Nominal Value | Test Method | |
Arc Resistance5 | PLC 6 | ASTM D495 | |
Comparative Tracking Index (CTI) | PLC 4 | UL 746 | |
High Amp Arc Ignition (HAI)6 | PLC 4 | UL 746 | |
High Voltage Arc Tracking Rate (HVTR) | PLC 3 | UL 746 | |
Hot-wire Ignition (HWI) | PLC 1 | UL 746 | |
| Flammability | Nominal Value | Test Method | |
Flame Rating | UL 94 | ||
0.25 mm | V-0 | ||
1.2 mm | 5VA |