Physical Properties | Metric | English | Comments |
---|
Specific Gravity | 1.27 g/cc | 1.27 g/cc | ASTM D792 |
Density | 1.27 g/cc | 0.0459 lb/in³ | ISO 1183 |
Water Absorption | 0.25 % @Time 86400 sec | 0.25 % @Time 24.0 hour | ASTM D570 |
| 0.25 % @Time 86400 sec | 0.25 % @Time 24.0 hour | ISO 62-1 |
Moisture Absorption | 0.0100 - 0.0200 % | 0.0100 - 0.0200 % | Extrusion Blow Molding |
| 0.0200 % | 0.0200 % | Injection Molding |
| 0.200 % | 0.200 % | 23°C/50% RH/24 hrs; ISO 62-4 |
Moisture Absorption at Equilibrium | 0.70 % | 0.70 % | 23°C/50% RH; ISO 62-4 |
Water Absorption at Saturation | 1.25 % | 1.25 % | ASTM D570 |
| 1.25 % | 1.25 % | ISO 62-1 |
Viscosity | 13 cP @Load 5.00 kg, Temperature 360 °C | 13 cP @Load 11.0 lb, Temperature 680 °F | MVR cc/10 min; ISO 1133 |
Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm | 0.0050 - 0.0070 in/in @Thickness 0.126 in | SABIC method |
Linear Mold Shrinkage, Transverse | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm | 0.0050 - 0.0070 in/in @Thickness 0.126 in | SABIC method |
Melt Flow | 9.0 g/10 min @Load 6.60 kg, Temperature 337 °C | 9.0 g/10 min @Load 14.6 lb, Temperature 639 °F | ASTM D1238 |
|
|
|
|
Mechanical Properties | Metric | English | Comments |
---|
Hardness, Rockwell M | 106 | 106 | ISO 2039-2 |
| 109 | 109 | ASTM D785 |
Ball Indentation Hardness | 140 MPa | 20300 psi | H358/30; ISO 2039-1 |
Tensile Strength, Yield | 110 MPa | 16000 psi | 5 mm/min; ASTM D638 |
| 110 MPa | 16000 psi | 50 mm/min; ISO 527 |
| 115 MPa | 16700 psi | 50 mm/min; ASTM D638 |
Elongation at Break | 50 % | 50 % | 50 mm/min; ISO 527 |
| 60 % | 60 % | 5 mm/min; ASTM D638 |
| 60 % | 60 % | 50 mm/min; ASTM D638 |
Elongation at Yield | 6.0 % | 6.0 % | 50 mm/min; ISO 527 |
| 7.0 % | 7.0 % | 5 mm/min; ASTM D638 |
| 7.0 % | 7.0 % | 50 mm/min; ASTM D638 |
Tensile Modulus | 3.20 GPa | 464 ksi | 1 mm/min; ISO 527 |
| 3.35 GPa | 486 ksi | 5 mm/min; ASTM D638 |
Flexural Strength | 160 MPa | 23200 psi | yld, 2.6 mm/min, 100 mm span; ASTM D790 |
| 160 MPa | 23200 psi | yield, 2 mm/min; ISO 178 |
| 165 MPa | 23900 psi | yld, 1.3 mm/min, 50 mm span; ASTM D790 |
Flexural Modulus | 3.20 GPa | 464 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 3.30 GPa | 479 ksi | 2 mm/min; ISO 178 |
| 3.40 GPa | 493 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
Poissons Ratio | 0.36 | 0.36 | ASTM E132 |
Izod Impact Notched | 53.0 J | 39.1 ft-lb | ASTM D256 |
| 50.0 J @Temperature -30.0 °C | 36.9 ft-lb @Temperature -22.0 °F | ASTM D256 |
| 1335 J @Thickness 3.20 mm | 984.6 ft-lb @Thickness 0.126 in | reverse notched; ASTM D256 |
Izod Impact, Unnotched | 18.0 J/cm | 33.7 ft-lb/in | ASTM D4812 |
| 15.4 J/cm @Temperature -30.0 °C | 28.9 ft-lb/in @Temperature -22.0 °F | ASTM D4812 |
Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1A |
| 6.00 kJ/m² @Temperature -30.0 °C | 2.86 ft-lb/in² @Temperature -22.0 °F | 80*10*4; ISO 180/1A |
Izod Impact, Unnotched (ISO) | NB | NB | 80*10*4; ISO 180/1U |
| NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | 80*10*4; ISO 180/1U |
Charpy Impact, Notched | 0.400 J/cm² | 1.90 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| 0.400 J/cm² @Temperature -30.0 °C | 1.90 ft-lb/in² @Temperature -22.0 °F | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
Gardner Impact | 36.0 J | 26.6 ft-lb | ASTM D3029 |
Taber Abrasion, mg/1000 Cycles | 10 | 10 | CS-17, 1 kg; ASTM D1044 |
|
|
|
|
Electrical Properties | Metric | English | Comments |
---|
Arc Resistance | 120 - 180 sec | 120 - 180 sec | ASTM D495 |
Comparative Tracking Index | 100 - 175 V | 100 - 175 V | UL 746A |
Hot Wire Ignition, HWI | 30 - 60 sec @Thickness >=0.750 mm | 30 - 60 sec @Thickness >=0.0295 in | UL 746A |
| 60 - 120 sec @Thickness >=3.00 mm | 60 - 120 sec @Thickness >=0.118 in | UL 746A |
High Amp Arc Ignition, HAI | 0.00 - 15 arcs @Thickness >=0.750 mm | 0.00 - 15 arcs @Thickness >=0.0295 in | UL 746A |
| 15 - 30 arcs @Thickness >=3.00 mm | 15 - 30 arcs @Thickness >=0.118 in | UL 746A |
High Voltage Arc-Tracking Rate, HVTR | 25.4 - 80.0 mm/min | 1.00 - 3.15 in/min | UL 746A |
|
|
|
|
Thermal Properties | Metric | English | Comments |
---|
CTE, linear, Parallel to Flow | 52.0 µm/m-°C @Temperature -20.0 - 150 °C | 28.9 µin/in-°F @Temperature -4.00 - 302 °F | ISO 11359-2 |
| 56.0 µm/m-°C @Temperature -20.0 - 150 °C | 31.1 µin/in-°F @Temperature -4.00 - 302 °F | ASTM E831 |
CTE, linear, Transverse to Flow | 52.0 µm/m-°C @Temperature -20.0 - 150 °C | 28.9 µin/in-°F @Temperature -4.00 - 302 °F | ISO 11359-2 |
| 54.0 µm/m-°C @Temperature -20.0 - 150 °C | 30.0 µin/in-°F @Temperature -4.00 - 302 °F | ASTM E831 |
Thermal Conductivity | 0.220 W/m-K | 1.53 BTU-in/hr-ft²-°F | ASTM C177 |
| 0.220 W/m-K | 1.53 BTU-in/hr-ft²-°F | ISO 8302 |
Hot Ball Pressure Test | 125 °C | 257 °F | PASS; IEC 60695-10-2 |
Deflection Temperature at 0.46 MPa (66 psi) | 209 °C | 408 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 207 °C @Thickness 3.20 mm | 405 °F @Thickness 0.126 in | unannealed; ASTM D648 |
| 210 °C @Thickness 6.40 mm | 410 °F @Thickness 0.252 in | unannealed; ASTM D648 |
Deflection Temperature at 1.8 MPa (264 psi) | 192 °C | 378 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 190 °C @Thickness 3.20 mm | 374 °F @Thickness 0.126 in | unannealed; ASTM D648 |
| 201 °C @Thickness 6.40 mm | 394 °F @Thickness 0.252 in | unannealed; ASTM D648 |
Vicat Softening Point | 211 °C | 412 °F | Rate B/50; ASTM D1525 |
| 211 °C | 412 °F | Rate B/50; ISO 306 |
| 212 °C | 414 °F | Rate B/120; ISO 306 |
| 215 °C | 419 °F | Rate A/50; ISO 306 |
UL RTI, Electrical | 170 °C | 338 °F | UL 746B |
UL RTI, Mechanical with Impact | 170 °C | 338 °F | UL 746B |
UL RTI, Mechanical without Impact | 170 °C | 338 °F | UL 746B |
Flammability, UL94 | V-2 @Thickness >=0.400 mm | V-2 @Thickness >=0.0157 in | UL 94 |
| V-0 @Thickness >=0.750 mm | V-0 @Thickness >=0.0295 in | UL 94 |
| 5VA @Thickness >=3.00 mm | 5VA @Thickness >=0.118 in | UL 94 |
Smoke Density | 0.70 | 0.70 | Flaming, Ds 4 min; ASTM E662 |
Oxygen Index | 47 % | 47 % | ASTM D2863 |
| 47 % | 47 % | ISO 4589 |
|
|
|
|
Processing Properties | Metric | English | Comments |
---|
Nozzle Temperature | 345 - 405 °C | 653 - 761 °F |
|
Zone 1 | 325 - 350 °C | 617 - 662 °F | Extrusion Blow Molding |
Zone 2 | 330 - 355 °C | 626 - 671 °F | Extrusion Blow Molding |
| 340 - 405 °C | 644 - 761 °F |
|
Zone 3 | 330 - 355 °C | 626 - 671 °F | Extrusion Blow Molding |
| 345 - 415 °C | 653 - 779 °F |
|
Zone 4 | 330 - 355 °C | 626 - 671 °F | Extrusion Blow Molding |
Zone 5 | 330 - 355 °C | 626 - 671 °F |
|
Die Temperature | 325 - 355 °C | 617 - 671 °F | Extrusion Blow Molding |
Melt Temperature | 320 - 355 °C | 608 - 671 °F | Extrusion Blow Molding |
| 350 - 410 °C | 662 - 770 °F | Injection Molding |
Head Temperature | 330 - 355 °C | 626 - 671 °F | Zone 6 - Top Temperature |
| 330 - 355 °C | 626 - 671 °F | Zone 7 - Bottom Temperature |
Mold Temperature | 65.0 - 175 °C | 149 - 347 °F |
|
| 135 - 180 °C | 275 - 356 °F |
|
Drying Temperature | 140 - 150 °C | 284 - 302 °F | Extrusion Blow Molding |
| 150 °C | 302 °F | Injection Molding |
Dry Time | 4.00 - 6.00 hour | 4.00 - 6.00 hour | Injection Molding |
| 4.00 - 6.00 hour | 4.00 - 6.00 hour | Extrusion Blow Molding |
| 24.0 hour | 24.0 hour | Cumulative; Injection Molding |
| 24.0 hour | 24.0 hour | Cumulative; Extrusion Blow Molding |
Back Pressure | 0.300 - 0.700 MPa | 43.5 - 102 psi |
|
Shot Size | 40 - 60 % | 40 - 60 % |
|
Vent Depth | 0.00250 - 0.00760 cm | 0.000984 - 0.00299 in |
|
Screw Speed | 10 - 70 rpm | 10 - 70 rpm |
|
|
|
|
|
Descriptive Properties |
|
|
|
---|
Screw speed (Circumferential speed) | 0.2-0.3 m/s |
|
|