| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.27 g/cc | 1.27 g/cc | ASTM D792 |
| Density | 1.27 g/cc | 0.0459 lb/in³ | *** 1183 |
| Water Absorption | 0.25 % @Time 86400 sec | 0.25 % @Time 24.0 hour | ASTM D570 |
| Moisture Absorption | 0.0200 % | 0.0200 % | Injection Molding |
| 0.700 % | 0.700 % | 23°C / 50% RH; *** 62 | |
| Water Absorption at Saturation | 1.25 % | 1.25 % | ASTM D570 |
| 1.25 % | 1.25 % | *** 62-1 | |
| Viscosity | 13 cP @Load 5.00 kg, Temperature 340 °C | 13 cP @Load 11.0 lb, Temperature 644 °F | MVR cc/10 min; *** 1133 |
| 25 cP @Load 5.00 kg, Temperature 360 °C | 25 cP @Load 11.0 lb, Temperature 680 °F | MVR cc/10 min; *** 1133 | |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | SABIC method |
| 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm | 0.0050 - 0.0070 in/in @Thickness 0.126 in | SABIC method | |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm | 0.0050 - 0.0070 in/in @Thickness 0.126 in | SABIC method |
| Melt Flow | 17.8 g/10 min @Load 6.60 kg, Temperature 337 °C | 17.8 g/10 min @Load 14.6 lb, Temperature 639 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 109 | 109 | ASTM D785 |
| Ball Indentation Hardness | 140 MPa | 20300 psi | H358/30; *** 2039-1 |
| Tensile Strength at Break | 85.0 MPa | 12300 psi | 50 mm/min; *** 527 |
| 105 MPa | 15200 psi | 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 105 MPa | 15200 psi | 50 mm/min; *** 527 |
| 110 MPa | 16000 psi | 5 mm/min; ASTM D638 | |
| Elongation at Break | 60 % | 60 % | 5 mm/min; ASTM D638 |
| 60 % | 60 % | 50 mm/min; *** 527 | |
| Elongation at Yield | 6.0 % | 6.0 % | 50 mm/min; *** 527 |
| 7.0 % | 7.0 % | 5 mm/min; ASTM D638 | |
| Tensile Modulus | 3.20 GPa | 464 ksi | 1 mm/min; *** 527 |
| 3.59 GPa | 521 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 160 MPa | 23200 psi | yield, 2 mm/min; *** 178 |
| 165 MPa | 23900 psi | yld, 2.6 mm/min, 100 mm span; ASTM D790 | |
| 167 MPa | 24200 psi | yld, 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 3.30 GPa | 479 ksi | 2 mm/min; *** 178 |
| 3.52 GPa | 511 ksi | 2.6 mm/min, 100 mm span; ASTM D790 | |
| 3.55 GPa | 515 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact Notched | 32.0 J | 23.6 ft-lb | ASTM D256 |
| 35.0 J @Temperature -30.0 °C | 25.8 ft-lb @Temperature -22.0 °F | ASTM D256 | |
| 1174 J @Thickness 3.20 mm | 865.9 ft-lb @Thickness 0.126 in | reverse notched; ASTM D256 | |
| Izod Impact, Unnotched | 13.35 J/cm | 25.01 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (***) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; *** 180/1A |
| 5.00 kJ/m² @Temperature -30.0 °C | 2.38 ft-lb/in² @Temperature -22.0 °F | 80*10*4; *** 180/1A | |
| Izod Impact, Unnotched (***) | NB | NB | 80*10*4; *** 180/1U |
| NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | 80*10*4; *** 180/1U | |
| Charpy Impact, Notched | 0.300 J/cm² | 1.43 ft-lb/in² | Edgew 80*10*4 sp=62mm; *** 179/1eA |
| Gardner Impact | 33.0 J | 24.3 ft-lb | SABIC method |
| Dart Drop, Total Energy | 33.0 J | 24.3 ft-lb | ASTM D3763 |
| Taber Abrasion, mg/1000 Cycles | 10 | 10 | CS-17, 1 kg; ASTM D1044 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| 1.00e+17 ohm-cm | 1.00e+17 ohm-cm | ASTM D257 | |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | ROA; IEC 60093 |
| Dielectric Constant | 2.9 @Frequency 1.00e+6 Hz | 2.9 @Frequency 1.00e+6 Hz | IEC 60250 |
| 2.9 @Frequency 50.0 - 60.0 Hz | 2.9 @Frequency 50.0 - 60.0 Hz | IEC 60250 | |
| 3.15 @Frequency 1000 Hz | 3.15 @Frequency 1000 Hz | ASTM D150 | |
| Dielectric Strength | 16.0 kV/mm @Thickness 3.20 mm | 406 kV/in @Thickness 0.126 in | in oil; IEC 60243-1 |
| 25.0 kV/mm @Thickness 1.60 mm | 635 kV/in @Thickness 0.0630 in | in oil; IEC 60243-1 | |
| 27.9 kV/mm @Thickness 1.60 mm | 709 kV/in @Thickness 0.0630 in | in oil; ASTM D149 | |
| 32.6 kV/mm @Thickness 1.60 mm | 828 kV/in @Thickness 0.0630 in | in air; ASTM D149 | |
| 33.0 kV/mm @Thickness 0.800 mm | 838 kV/in @Thickness 0.0315 in | in oil; IEC 60243-1 | |
| Dissipation Factor | 0.00050 @Frequency 50.0 - 60.0 Hz | 0.00050 @Frequency 50.0 - 60.0 Hz | IEC 60250 |
| 0.0013 @Frequency 1000 Hz | 0.0013 @Frequency 1000 Hz | ASTM D150 | |
| 0.0025 @Frequency 2.45e+9 Hz | 0.0025 @Frequency 2.45e+9 Hz | ASTM D150 | |
| 0.0025 @Frequency 2.45e+9 Hz | 0.0025 @Frequency 2.45e+9 Hz | IEC 60250 | |
| 0.0060 @Frequency 1.00e+6 Hz | 0.0060 @Frequency 1.00e+6 Hz | IEC 60250 | |
| Comparative Tracking Index | 100 V | 100 V | IEC 60112 |
| 150 V | 150 V | IEC 60112 | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 50.0 µm/m-°C @Temperature 23.0 - 150 °C | 27.8 µin/in-°F @Temperature 73.4 - 302 °F | *** 11359-2 |
| 55.0 µm/m-°C @Temperature -40.0 - 150 °C | 30.6 µin/in-°F @Temperature -40.0 - 302 °F | ASTM E831 | |
| CTE, linear, Transverse to Flow | 50.0 µm/m-°C @Temperature 23.0 - 150 °C | 27.8 µin/in-°F @Temperature 73.4 - 302 °F | *** 11359-2 |
| 55.0 µm/m-°C @Temperature -40.0 - 150 °C | 30.6 µin/in-°F @Temperature -40.0 - 302 °F | ASTM E831 | |
| Thermal Conductivity | 0.210 W/m-K | 1.46 BTU-in/hr-ft²-°F | *** 8302 |
| 0.220 W/m-K | 1.53 BTU-in/hr-ft²-°F | ASTM C177 | |
| Hot Ball Pressure Test | 125 °C | 257 °F | PASS; IEC 60695-10-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 200 °C | 392 °F | Edgew 120*10*4 sp=100mm; *** 75/Be |
| 205 °C @Thickness 3.20 mm | 401 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| 207 °C @Thickness 6.40 mm | 405 °F @Thickness 0.252 in | unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | Edgew 120*10*4 sp=100mm; *** 75/Ae |
| 190 °C | 374 °F | Flatw 80*10*4 sp=64mm; *** 75/Af | |
| 197 °C @Thickness 3.20 mm | 387 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| 198 °C @Thickness 6.40 mm | 388 °F @Thickness 0.252 in | unannealed; ASTM D648 | |
| Vicat Softening Point | 211 °C | 412 °F | Rate B/50; *** 306 |
| 212 °C | 414 °F | Rate B/120; *** 306 | |
| 215 °C | 419 °F | Rate A/50; *** 306 | |
| 218 °C | 424 °F | Rate B/50; ASTM D1525 | |
| Oxygen Index | 44 % | 44 % | ASTM D2863 |
| 47 % | 47 % | *** 4589 | |
| Glow Wire Flammability Index | 960 °C @Thickness 3.20 mm | 1760 °F @Thickness 0.126 in | IEC 60695-2-12 |
| Processing Properties | Metric | English | Comments |
| Nozzle Temperature | 345 - 400 °C | 653 - 752 °F | |
| Zone 2 | 340 - 400 °C | 644 - 752 °F | |
| Zone 3 | 345 - 400 °C | 653 - 752 °F | |
| Melt Temperature | 350 - 400 °C | 662 - 752 °F | Injection Molding |
| Mold Temperature | 135 - 165 °C | 275 - 329 °F | |
| Drying Temperature | 150 °C | 302 °F | Injection Molding |
| Dry Time | 4.00 - 6.00 hour | 4.00 - 6.00 hour | Injection Molding |
| 24.0 hour | 24.0 hour | Cumulative; Injection Molding | |
| Back Pressure | 0.300 - 0.700 MPa | 43.5 - 102 psi | |
| Shot Size | 40 - 60 % | 40 - 60 % | |
| Vent Depth | 0.00250 - 0.00760 cm | 0.000984 - 0.00299 in | |
| Screw Speed | 40 - 70 rpm | 40 - 70 rpm |
本公司长期销售沙伯基础 PEI，ABS，ASA，EVA，PA6，PBT，PE，PBT，PET，PMMA，POM，PS，PP，PU，PES，PC料等多种牌号
我司产品均可提供详细物性表(英文和中文版)相关资料；可开13%增值税发票；免费为客户分析样版并提供原料型号咨询服务(可免费帮客户翻译英文资料)；如需试料、了解产品相关信息及当日报价，敬请来电、竭诚为您服务！
为您推荐
-
PEI SF2350 沙伯基础(原GE) 高流动性 ¥90.00
-
-
-
PEI XP050 沙伯基础(原GE) 阻燃 泡沫 ¥90.00
-
-
PEI foam XP080 沙伯基础(原GE) 阻燃 ¥90.00
-
PEI foam XP110 沙伯基础(原GE) 阻燃 ¥90.00
-
PES J1000 沙伯基础(原GE) 注射成型 ¥90.00
-
PES J1000AE 沙伯基础(原GE) 易于成型 ¥90.00
-
-
-
PES JX09403J 沙伯基础(原GE) 低萃取物 ¥90.00
在线问
产品参数
- 否
- 美国
- 沙伯基础(原GE)
- MD131
- 品牌经销
- 标准料
- 注塑级
- 标准级
- 汽车部件、 电子电器部件、 运动器材、 家电部件、 电动工具配件