Density | 1.39 | g/cm | *** 1183 |
Melt Volume-Flow Rate (MVR)(190°C/2.16 kg) | 20 | cm/10min | *** 1133 |
Molding Shrinkage | *** 294-4 | ||
Across Flow | 1.6 | % | |
Flow | 1.9 | % |
| Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus | 2530 | MPa | *** 527-2/1A |
Tensile Stress(Yield) | 56.0 | MPa | *** 527-2/1A/50 |
Tensile Strain(Yield) | 9.0 | % | *** 527-2/1A/50 |
Nominal Tensile Strain at Break | 11 | % | *** 527-2/1A/50 |
Flexural Modulus(23°C) | 2500 | MPa | *** 178 |
Flexural Stress(3.5% Strain) | 67.0 | MPa | *** 178 |
| Impact | Nominal Value | Unit | Test Method |
Charpy Notched Impact Strength | *** 179/1eA | ||
-30°C | 3.7 | kJ/m | |
23°C | 3.7 | kJ/m |
| Thermal | Nominal Value | Unit | Test Method |
Heat Deflection Temperature(1.8 MPa, Unannealed) | 90.0 | °C | *** 75-2/A |
Vicat Softening Temperature | 161 | °C | *** 306/B50 |
Melting Temperature2 | 167 | °C | *** 11357-3 |
POM塑料特性
1、POM具有很低的摩擦系数和很好的几何稳定性，特别适合于制作齿轮和轴承。
2、POM具有***特性，因此还用于管道器件（管道阀门、泵壳体），草坪设备等。
3、POM是一种坚韧有弹性的材料，即使在低温下仍有很好的抗蠕变特性、几何稳定性和抗冲击特性。
4、POM的高结晶程度导致它有相当高的收缩率，可高达到2%~3.5%。对于各种不同的增强型材料有不同的收缩率。
5、POM属结晶性塑料，熔点明显，一旦达到熔点，熔体粘度迅速下降。