Density | 1.37 | g/cm | ISO 1183 |
Melt Mass-Flow Rate (MFR)(190°C/2.16 kg) | 6.8 | g/10 min | ISO 1133 |
Melt Volume-Flow Rate (MVR)(190°C/2.16 kg) | 5.8 | cm/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
Tensile Stress(Yield) | 45.0 | MPa | ISO 527-2/50 |
Tensile Strain | ISO 527-2/50 | ||
Yield | 11 | % | |
Break | 65 | % | |
Flexural Modulus3 | 1700 | MPa | ISO 178 |
Flexural Stress3 | 61.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
Charpy Notched Impact Strength(23°C) | 12 | kJ/m | ISO 179 |
Charpy Unnotched Impact Strength(23°C) | No Break | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
Heat Deflection Temperature(1.8 MPa, Unannealed) | 82.0 | °C | ISO 75-2/A |
Melting Temperature | 166 | °C | ISO 11357-3 |
| Flammability | Nominal Value | Test Method | |
Flame Rating(0.8 mm) | HB | UL 94 |