YUPLENE B391M高流动高抗冲PP韩国SK
¥18.00
YUPLENE B393G超高流动尺寸稳定PP韩国SK
¥18.00
韩国SK YUPLENE B920F耐冲击高流动PP
¥18.00
YUPLENE B920G增韧高抗冲PP韩国SK
¥18.00
YUPLENE BH3500高耐热高抗冲PP韩国SK
¥18.00
韩国SK PP YUPLENE BH3800高抗冲
¥18.00
YUPLENE B391G高抗冲高流动PP韩国SK
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 40 | g/10 min | ASTM D1238 |
Spiral Flow | > 80.0 | cm | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
Rockwell Hardness (R-Scale) | 90 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
Tensile Strength (Yield) | 25.5 | MPa | ASTM D638 |
Tensile Elongation (Break) | <500 | % | ASTM D638 |
Flexural Modulus | 1270 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
Notched Izod Impact | ASTM D256 | ||
-20°C | 49 | J/m | |
23°C | 74 | J/m |
| Aging | Nominal Value | Unit | Test Method |
Accelerated Oven Aging - in Air (150°C) | 15.0 | day | ASTM D3012 |
| Thermal | Nominal Value | Unit | Test Method |
Vicat Softening Temperature | 150 | °C | ASTM D1525 |
Heat Deflection Temperature | 110 | °C | ASTM D648 |
| Additional Information | Nominal Value | Unit | Test Method |
DuPont Impact Strength (-10°C) | > 1.96 | J | ASTM D2794 |
在线问