GRIVORY XE4164瑞士EMS耐化学30%玻纤PPA
Density | 1.40 | -- | g/cm | ISO 1183 |
Molding Shrinkage | ISO 294-4 | |||
Across Flow | 0.70 | -- | % | |
Flow | 0.20 | -- | % | |
Water Absorption | ISO 62 | |||
Saturation, 23°C | 3.5 | -- | % | |
Equilibrium, 23°C, 50% RH | 1.6 | -- | % | |
Hardness | Dry | Conditioned | Unit | Test Method |
Ball Indentation Hardness | 271 | 264 | MPa | ISO 2039-1 |
Mechanical | Dry | Conditioned | Unit | Test Method |
Tensile Modulus | 10500 | 10500 | MPa | ISO 527-2 |
Tensile Stress(Break) | 150 | 150 | MPa | ISO 527-2 |
Tensile Strain(Break) | 1.8 | 1.8 | % | ISO 527-2 |
Impact | Dry | Conditioned | Unit | Test Method |
Charpy Notched Impact Strength | ISO 179/1eA | |||
-30°C | 8.0 | 8.0 | kJ/m | |
23°C | 10 | 10 | kJ/m | |
Charpy Unnotched Impact Strength | ISO 179/1eU | |||
-30°C | 35 | 35 | kJ/m | |
23°C | 40 | 40 | kJ/m |
Thermal | Dry | Conditioned | Unit | Test Method |
Heat Deflection Temperature | ||||
1.8 MPa, Unannealed | 275 | -- | °C | ISO 75-2/A |
8.0 MPa, Unannealed | 140 | -- | °C | ISO 75-2/C |
Continuous Use Temperature | ||||
--2 | 150 | -- | °C | ISO 2578 |
--3 | 250 | -- | °C | Internal Method |
Melting Temperature4 | 316 | -- | °C | ISO 11357-3 |
CLTE | ISO 11359-2 | |||
Flow | 2.0E-5 | -- | cm/cm/°C | |
Transverse | 7.0E-5 | -- | cm/cm/°C |
Electrical | Dry | Conditioned | Unit | Test Method |
Surface Resistivity | -- | 1.0E+10 | ohms | IEC 60093 |
Volume Resistivity | 1.0E+11 | 1.0E+11 | ohms·cm | IEC 60093 |
Electric Strength | 32 | 30 | kV/mm | IEC 60243-1 |
Comparative Tracking Index | -- | 600 | V | IEC 60112 |
Flammability | Dry | Conditioned | Unit | Test Method |
Flammability Classification | IEC 60695-11-10, -20 | |||
0.40 mm | HB | -- | ||
1.5 mm | HB | -- |
改性PPA塑料的热变形温度高达300℃以上,连续使用温度可达170℃,能满足您所需的短期和长期的热性能。它可在宽广的温度范围内和高湿度环境中保持其优越的机械性特性—强度、硬度、耐疲劳性及抗蠕变性。增韧吕级PPA结合优越的韧度与一定范围的硬度和柔性,在扣件中要求一次性使用的刚性、以及重复性使用中挠屈性的良好选择。同时提供特殊品级的产品应用于可喷涂和可电镀的表面,防火性性要求的应用