代理美国杜邦PPA Zytel HTN FR42G30NH无卤阻燃环保
Density | 1.45 | g/cm | *** 1183 |
Biobased Carbon Content | 21 | % | *** 16620-2 |
Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus | 10600 | MPa | *** 527-2 |
Tensile Stress(Break) | 138 | MPa | *** 527-2 |
Tensile Strain(Break) | 1.8 | % | *** 527-2 |
Flexural Modulus | 11200 | MPa | *** 178 |
Flexural Stress | 216 | MPa | *** 178 |
Poisson's Ratio | 0.34 | ||
Impact | Nominal Value | Unit | Test Method |
Charpy Notched Impact Strength(23°C) | 7.0 | kJ/m | *** 179/1eA |
Charpy Unnotched Impact Strength(23°C) | 46 | kJ/m | *** 179/1eU |
Thermal | Nominal Value | Unit | Test Method |
Melting Temperature2 | 315 | °C | *** 11357-3 |
RTI Elec | UL 746 | ||
0.40 mm | 130 | °C | |
1.5 mm | 130 | °C | |
3.0 mm | 130 | °C | |
RTI Imp | UL 746 | ||
0.40 mm | 115 | °C | |
1.5 mm | 115 | °C | |
3.0 mm | 120 | °C | |
RTI Str | UL 746 | ||
0.40 mm | 125 | °C | |
1.5 mm | 125 | °C | |
3.0 mm | 130 | °C |
Electrical | Nominal Value | Unit | Test Method |
Comparative Tracking Index (CTI)(3.00 mm) | PLC 0 | UL 746 | |
Comparative Tracking Index | 600 | V | IEC 60112 |